SARLINK ME-2340B-01 BLK是一种通用热塑性弹性体,用于汽车造型应用,包括车身。SARLINK ME-2340B-01 BLK是一种低硬度、低密度、紫外线稳定的等级,具有优异的压缩永久变形和耐化学腐蚀性。 Sarlink ME-2340B-01 BLK is a general purpose thermoplastic elastomer used in automotive molding applications, including exterior. Sarlink ME-2340B-01 BLK is a low hardness, low density, UV stabilized grade exhibiting superior compression set and chemical resistance. |
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ISO 868 | ||
邵氏 A,1 秒,注塑成型 Shore A, 1 second, injection molding |
41 | ISO 868 | |
邵氏 A,5 秒,注塑成型 Shore A, 5 seconds, injection molding |
40 | ISO 868 | |
邵氏 A,15 秒,注塑成型 Shore A, 15 seconds, injection molding |
39 | ISO 868 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 2 |
ISO 37 | ||
TD,断裂 TD, fracture |
5.40 | MPa | ISO 37 |
MD,断裂 MD, fracture |
3.40 | MPa | ISO 37 |
拉伸应变 Tensile strain 2 |
ISO 37 | ||
TD,断裂 TD, fracture |
% | ISO 37 | |
流量,断裂 Flow rate, fracture |
% | ISO 37 | |
撕裂强度 tear strength 3 |
ISO 34-1 | ||
TD TD |
kN/m | ISO 34-1 | |
MD MD |
kN/m | ISO 34-1 | |
压缩形变 Compression deformation 4 |
ISO 815 | ||
23℃,22 hr 23℃,22 hr |
% | ISO 815 | |
70℃,22 hr 70℃,22 hr |
% | ISO 815 | |
90℃,70 hr 90℃,70 hr |
% | ISO 815 | |
125℃,70 hr 125℃,70 hr |
% | ISO 815 | |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 The rate of change in tensile strength in air 5 |
ISO 188 | ||
TD:110℃,1008 hr TD:110℃,1008 hr |
% | ISO 188 | |
MD:110℃,1008 hr MD:110℃,1008 hr |
% | ISO 188 | |
TD:100% 应变 110℃,1008 hr TD: 100% strain at 110 ℃, 1008 hr |
% | ISO 188 | |
MD:100% 应变 110℃,1008 hr MD: 100% strain at 110 ℃, 1008 hr |
% | ISO 188 | |
TD:125℃,168 hr TD:125℃,168 hr |
% | ISO 188 | |
MD:125℃,168 hr MD:125℃,168 hr |
% | ISO 188 | |
TD:100% 应变 125℃,168 hr TD: 100% strain 125 ℃, 168 hr |
% | ISO 188 | |
MD:100% 应变 125℃,168 hr MD: 100% strain 125 ℃, 168 hr |
% | ISO 188 | |
在空气中断裂时拉伸应力变化 Changes in tensile stress during fracture in air 5 |
ISO 188 | ||
TD:110℃,1008 hr TD:110℃,1008 hr |
% | ISO 188 | |
流量:110℃,1008 hr Flow rate: 110 ℃, 1008 hr |
% | ISO 188 | |
TD:125℃,168 hr TD:125℃,168 hr |
% | ISO 188 | |
流量:125℃,168 hr Flow rate: 125 ℃, 168 hr |
% | ISO 188 | |
空气中邵氏硬度的变化率 The rate of change of Shore hardness in air |
ISO 188 | ||
邵氏 A,110℃,1008 hr Shore A, 110 ℃, 1008 hr 6 |
ISO 188 | ||
邵氏 A,110℃,1008 hr Shore A, 110 ℃, 1008 hr 7 |
ISO 188 | ||
邵氏 A,110℃,1008 hr Shore A, 110 ℃, 1008 hr 8 |
ISO 188 | ||
邵氏 A,125℃,168 hr Shaw A, 125 ℃, 168 hr 6 |
ISO 188 | ||
邵氏 A,125℃,168 hr Shaw A, 125 ℃, 168 hr 7 |
ISO 188 | ||
邵氏 A,125℃,168 hr Shaw A, 125 ℃, 168 hr 8 |
ISO 188 | ||
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ISO 1183 | |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
g/10min | ASTM D1238 | |
熔体表观粘度 Apparent viscosity of melt |
|||
200℃,206 sec^-1 200℃,206 sec^-1 |
Pa·s | ASTM D3835 | |
特殊值 Special value |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
TD,100% 应变 TD, 100% strain |
MPa | ISO 37 | |
MD,100% 应变 MD, 100% strain |
MPa | ISO 37 |
备注 |
---|
2 类型 1, 510 mm/min |
3 B 方法,直角形试样(不割口), 510 mm/min |
4 类型 A |
5 类型 1 |
6 15 sec |
7 5 sec |
8 1 sec |
【新闻资讯】查看全部
国龙再生,迈入“食品级再生塑料”新征程,探寻塑料行业新标杆
2021-07-26 搜料网资讯: 近日,美国食品药品监督管理局(Food and Drug Administration, FDA) 向国龙再生资源发展有限公司发出无异议函(LNO)。 确认其再生PET片材生产体系已经正式通过美国FDA审核认证,这 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |