牌号简介 About |
---|
Sarlink RV-2250D BLK 111是一种高性能热塑性弹性体,用于各种运输应用。SARLINK RV-2250D BLK 111是一种高硬度、中等密度的挤压级产品,具有耐阳光和紫外线吸收特性。 Sarlink RV-2250D BLK 111 is a high performance thermoplastic elastomer used in a variety of transportation applications. Sarlink RV-2250D BLK 111 is a high hardness medium density extrusion grade that exhibits sunlight resistance and UV absorbing characteristics. |
技术参数 Technical Data | |||
---|---|---|---|
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 2 |
ISO 37 | ||
断裂 fracture |
12.6 | MPa | ISO 37 |
MD,断裂 MD, fracture |
15.2 | MPa | ISO 37 |
拉伸应变 Tensile strain 2 |
ISO 37 | ||
断裂 fracture |
720 | % | ISO 37 |
流量,断裂 Flow rate, fracture |
360 | % | ISO 37 |
撕裂强度 tear strength 3 |
ISO 34-1 | ||
TD TD |
150 | kN/m | ISO 34-1 |
MD MD |
kN/m | ISO 34-1 | |
压缩形变 Compression deformation 4 |
ISO 815 | ||
23℃,22 hr 23℃,22 hr |
% | ISO 815 | |
70℃,22 hr 70℃,22 hr |
% | ISO 815 | |
90℃,70 hr 90℃,70 hr |
% | ISO 815 | |
125℃,70 hr 125℃,70 hr |
% | ISO 815 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ISO 868 | ||
邵氏 D,1 秒,注塑成型 Shore D, 1 second, injection molding |
ISO 868 | ||
邵氏 D,5 秒,注塑成型 Shore D, 5 seconds, injection molding |
ISO 868 | ||
邵氏 D,15 秒,注塑成型 Shore D, 15 seconds, injection molding |
ISO 868 | ||
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 The rate of change in tensile strength in air 5 |
ISO 188 | ||
TD:110℃,1008 hr TD:110℃,1008 hr |
% | ISO 188 | |
MD:110℃,1008 hr MD:110℃,1008 hr |
% | ISO 188 | |
TD:100% 应变 110℃,1008 hr TD: 100% strain at 110 ℃, 1008 hr |
% | ISO 188 | |
MD:100% 应变 110℃,1008 hr MD: 100% strain at 110 ℃, 1008 hr |
% | ISO 188 | |
TD:125℃,168 hr TD:125℃,168 hr |
% | ISO 188 | |
MD:125℃,168 hr MD:125℃,168 hr |
% | ISO 188 | |
TD:100% 应变 125℃,168 hr TD: 100% strain 125 ℃, 168 hr |
% | ISO 188 | |
MD:100% 应变 125℃,168 hr MD: 100% strain 125 ℃, 168 hr |
% | ISO 188 | |
在空气中断裂时拉伸应力变化 Changes in tensile stress during fracture in air 5 |
ISO 188 | ||
TD:110℃,1008 hr TD:110℃,1008 hr |
% | ISO 188 | |
流量:110℃,1008 hr Flow rate: 110 ℃, 1008 hr |
% | ISO 188 | |
TD:125℃,168 hr TD:125℃,168 hr |
% | ISO 188 | |
流量:125℃,168 hr Flow rate: 125 ℃, 168 hr |
% | ISO 188 | |
空气中邵氏硬度的变化率 The rate of change of Shore hardness in air |
ISO 188 | ||
支撐 D,110℃,1008 hr Support D, 110 ℃, 1008 hr 6 |
ISO 188 | ||
支撐 D,110℃,1008 hr Support D, 110 ℃, 1008 hr 8 |
ISO 188 | ||
支撐 D,125℃,168 hr Support D, 125 ℃, 168 hr 6 |
ISO 188 | ||
支撐 D,125℃,168 hr Support D, 125 ℃, 168 hr 7 |
ISO 188 | ||
支撐 D,125℃,168 hr Support D, 125 ℃, 168 hr 8 |
ISO 188 | ||
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ISO 1183 | |
熔体质量流动速率 Melt Flow Rate |
|||
200℃,5.0kg 200℃,5.0kg |
g/10min | ASTM D1238 | |
熔体表观粘度 Apparent viscosity of melt |
|||
200℃,206 sec^-1 200℃,206 sec^-1 |
Pa·s | ASTM D3835 | |
特殊值 Special value |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
TD,100% 应变 TD, 100% strain |
MPa | ISO 37 | |
MD,100% 应变 MD, 100% strain |
MPa | ISO 37 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 类型 1, 20 in/min |
3 B 方法,直角形试样(不割口), 20 in/min |
4 类型 A |
5 类型 1 |
6 1 sec |
7 15 sec |
8 5 sec |
【新闻资讯】查看全部
“塑战速决”:应对塑料污染有三大“技术流”
2018-06-06 今年世界环境日主题是“塑战速决”,呼吁全球关注一次性塑料污染。面对这一全球性挑战,各国研究人员在呼吁提高公民环保意识的同时,也试图运用技术手段减少污染,提出“替代一批”“消耗一批”“转化一批”的技术路线。 纤维素替代 美国宾夕法尼亚州立大学研究人员开发出一种廉价的可降解生物材料,可用于替代包装中常用的塑料涂层。 研究人员介绍,这种材料源自木材或棉花中的纤维素浆以及从节肢和甲壳动物外骨骼中获得的壳聚糖。这两种生 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |