牌号简介 About |
---|
Durethan® BKV 40 H2.0 901510 含有40%的玻璃纤维增强的PA 6材料,用注射成型的方式进行加工,具有良好的热老化稳定性。 Durethan® BKV40H2.0 901510 (Dry) PA 6, 40 % glass fibers, injection molding, heat-aging stabilized Durethan® BKV40H2.0 901510 PA 6, 40 % glass fibers, injection molding, heat-aging stabilized Durethan® BKV40H2.0 901510 PA 6, 40 % glass fibers, injection molding, heat-aging stabilized |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.46 | g/cm³ | ASTM D792 |
密度 Density |
1.46 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
|||
TD:280℃,3.0 mm TD:280℃,3.0 mm 2 |
0.85 | % | ISO 2577 |
TD:120℃,3.0 mm,2 hrs TD:120℃,3.0 mm,2 hrs 3 |
0.070 | % | ISO 294-4 |
MD:280℃,3.0 mm MD:280℃,3.0 mm 2 |
0.16 | % | ISO 2577 |
MD:120℃,3.0 mm,2 hrs MD:120℃,3.0 mm,2 hrs 3 |
% | ISO 2577 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ 4 |
MPa | ASTM D638 | |
23℃ 23℃ |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
MPa | ASTM D638 | |
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2/5 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2/5 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ 5 |
MPa | ISO 178-A | |
23℃ 23℃ |
MPa | ASTM D790 | |
弯曲强度 bending strength 5 |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
3.50% 应变 3.50% strain |
MPa | ISO 178-A | |
23℃ 23℃ |
MPa | ISO 178 | |
弯曲应变 Bending strain 6 |
% | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eU | |
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-40℃,3.2mm -40℃,3.2mm |
J/m | ASTM D256 | |
23℃,3.2mm 23℃,3.2mm |
J/m | ASTM D256 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/1A | ||
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,4.0 mm 1.8 MPa, unannealed, 4.0 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火,4.0 mm 0.45 MPa, unannealed, 4.0 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
|||
B120 B120 |
℃ | ISO 306/B120 | |
熔融温度 Melting temperature 7 |
℃ | ISO 11357-3 | |
相对温度指数 Relative temperature index |
|||
电气性能,1.50 mm Electrical performance, 1.50 mm |
℃ | UL 746 | |
强度机械性能,1.50 mm Strength mechanical performance, 1.50 mm |
℃ | UL 746 | |
冲击机械性能,1.50 mm Impact mechanical performance, 1.50 mm |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
|||
23℃ 23℃ |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
IEC 60243-1 | ||
23 ℃,1 mm 23 ℃,1 mm |
kV/mm | IEC 60243-1 | |
23 ℃,3 mm 23 ℃,3 mm |
kV/mm | IEC 60243-1 | |
介电常数 Dielectric constant 6 |
IEC 60250 | ||
23 ℃,50 Hz 23 ℃,50 Hz |
IEC 60250 | ||
23 ℃,1 MHz 23 ℃,1 MHz |
IEC 60250 | ||
相对电容率 Relative permittivity |
IEC 60250 | ||
23℃,100 Hz 23℃,100 Hz |
IEC 60250 | ||
23℃,1 MHz 23℃,1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
23℃,50 Hz 23℃,50 Hz |
IEC 60250 | ||
23℃,100 Hz 23℃,100 Hz |
IEC 60250 | ||
23℃,1 MHz 23℃,1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | ASTM D3638 | |
解决方案 A Solution A |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
1.60 mm 1.60 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
3.20 mm 3.20 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
|||
2.0 mm 2.0 mm |
℃ | IEC 60695-2-12 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
ISO Shortname ISO Shortname |
ISO 1874 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 150x150x3; MT 80°C; 400 Bar |
3 150x105x3mm, 80°C MT, 400 bar |
4 150x150x3 |
5 150x105x3mm |
6 0.039 in/min |
7 0.079 in/min |
8 Pull Rate: 2 mm/min; 50% RH |
9 2 mm/min |
10 10°C/min |
11 Tinfoil Electrodes |
【新闻资讯】查看全部
英国高调宣布25年内消灭一切塑料渣滓
2018-02-06 英国首相特雷莎・梅近日向塑料包装高调“宣战”:25年内消灭所有可避免的塑料垃圾。为实现这一目标,过去只在超市征收的5便士塑料袋消费税将被推广到英国所有商店,超市将为散装的食品增设无塑料包装通道,甚至还有提议称,由于咖啡杯盖子也含有塑料成分,因此将被征收25便士的“拿铁税”。 这份“新25年绿色计划”的“发令枪”才刚刚打响,大家像是赶时髦似地,踊跃加入这场“战役”。据英国广播公司(BBC)报道,不久前,英国最大零售企业玛莎百货就因过度包装花菜被民众吐槽:两片花菜、一个柠檬加上 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |