牌号简介 About |
---|
LL0220AA是以丁烯-1为共聚单体的线性低密度聚乙烯共聚物。LL0220AA是专门为生产手包和其他铸造拉伸薄膜,如定向带而开发的。它也可以作为低密度聚乙烯或低密度聚乙烯在铸造和吹塑薄膜应用中的混合伙伴。LL0220AA采用铸造挤压工艺加工具有以下优点:机械性能平衡好。良好的光学性能。贴附性能好。LL0220AA还可用作低压电力电缆绝缘或光纤护套的化合物。LL0220AA应在为LLDPE设计的机械中加工。铸造过程中的熔化温度范围通常为240°C-280°C,吹塑薄膜的贫混合物的熔化温度范围为165°C-215°C。LL0220AA应存放在50°C以下的干燥条件下,避免阳光直射。*LL0220AA适用于食品接触。 LL0220AA is a linear low density polyethylene copolymer containing butene-1 as a co-monomer. LL0220AA has been specially developed for production of hand wrap and other cast stretch films such as oriented tapes. It can also be used as a blending partner in LDPE or LLDPE in both cast and blown film applications. LL0220AA offers the following advantages when it processed by the cast extrusion process: Good balance of mechanical properties. Good optical properties. Good cling performance. LL0220AA also can be used as compounds for low voltage power cable insulation or fibre optic jacketing. LL0220AA should be processed in machinery designed for LLDPE. Melt temperature range in the cast process are normally 240°C-280°C and in lean blends for blown film are 165°C-215°C. LL0220AA should be stored in the dry condition below the 50°C and avoided from the exposure of direct sunlight. * LL0220AA is suitable for food contact. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.917 到 0.920 | g/cm³ | ASTM D2838 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
2.0 到 2.5 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
38 | µm | |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服 MD, yield |
10.0 | MPa | ASTM D882 |
TD,屈服 TD, yield |
9.00 | MPa | ASTM D882 |
MD,断裂 MD, fracture |
MPa | ASTM D882 | |
TD,断裂 TD, fracture |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂 MD, fracture |
% | ASTM D882 | |
TD,断裂 TD, fracture |
% | ASTM D882 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD:25 µm MD:25 µm |
g | ASTM D1922 | |
TD:25 µm TD:25 µm |
g | ASTM D1922 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45° 45° |
ASTM D2457 | ||
雾度 Haze |
% | ASTM D1003 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Blown Film Melt Temperature Blown Film Melt Temperature |
℃ | ||
|
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
塑料原料跌价 塑企如何出牌才干“不出局”?
2017-09-27 对于塑料制品企业来说,原材料成本在所有成本中占据着关键一席。今年7月后,塑料原料市场再次发起一波凶猛的涨势。不少企业认为,此番原料价格上涨将是行业“洗牌”的开始。那么,塑料制品企业如何出牌,才能不被“洗”出局? 塑料原料“金九”涨势强劲 聚丙烯是塑料产品的一种主要原材料,今年8月,它的价格便是步步高升,而在9月份,更是呈现出一种“不依不饶”的气势,业内人士称其“涨到怀疑人生”。据统计,每吨聚丙烯的价格从7月初的7900元涨至 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |