牌号简介 About |
---|
TAISOX 6130F是一种低密度聚乙烯材料,。 该产品在北美洲、欧洲或亚太地区有供货,加工方式为:吹塑成型。 TAISOX 6130F的主要特性有: 低收缩性 坚硬 美观 典型应用领域包括: 电影 涂覆应用 TAISOX® 6130F is a Low Density Polyethylene material. It is available in Asia Pacific, Europe, or North America for blow molding. Important attributes of TAISOX® 6130F are: Good Aesthetics Low Shrinkage Rigid Typical applications include: Coating Applications Film |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.924 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.80 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
50 | µm | |
薄膜厚度 film thickness |
1.2-4.7 mil (30-120 µ | ||
割线模量 Secant modulus |
ASTM D882 | ||
1% 正割,MD:50 µm,吹塑薄膜 1% secant, MD: 50 µ m, blow molded film |
186 | MPa | ASTM D882 |
1% 正割,TD:50 µm,吹塑薄膜 1% secant, TD: 50 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服,50 µm,吹塑薄膜 MD, yield, 50 µ m, blow molded film |
MPa | ASTM D882 | |
TD,屈服,50 µm,吹塑薄膜 TD, yield, 50 µ m, blow molded film |
MPa | ASTM D882 | |
MD,断裂,50 µm,吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
MPa | ASTM D882 | |
TD,断裂,50 µm,吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
断裂 fracture |
% | ASTM D638 | |
MD,断裂,50 µm,吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
% | ASTM D882 | |
TD,断裂,50 µm,吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
50 µm,吹塑薄膜 50 µ m, blow molded film |
g | ASTM D1709 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD:50 µm,吹塑薄膜 MD: 50 µ m, blow molded film |
g | ASTM D1922 | |
TD:50 µm,吹塑薄膜 TD: 50 µ m, blow molded film |
g | ASTM D1922 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
熔融温度 Melting temperature |
℃ | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,50.0 µm,吹塑薄膜 45 °, 50.0 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
50 µm,吹塑薄膜 50 µ m, blow molded film |
% | ASTM D1003 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
拉伸强度 tensile strength |
ASTM D638 | ||
屈服 yield |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
摩擦系数 friction coefficient |
|||
吹塑薄膜 Blown film |
ASTM D1894 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
塑料产业定价方式转变加速贸易商洗牌
2016-08-25 近两年来,随着期货市场的快速发展,以期货价格为现货贸易定价的点价模式在石化塑料领域快速发展,它改变了以往传统“背靠背”贸易方式的同时,也倒逼贸易商为上下游企业提供更多的贸易服务,进一步加速了贸易商洗牌。 点价模式盛行 所谓点价贸易是指买卖双方在交易过程中以约定的某个时段期货价格为基准,在此基础上加减一个升贴水来确定。从本质上讲,点价贸易并非期货交易,而是一 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |