牌号简介 About |
---|
PRL PC-HM-FR1-(color)-1是一种聚碳酸酯(PC)产品,含有的填充物为10% 玻璃纤维增强材料。 它可以通过注射成型进行加工,在北美洲有供货。 特性包括: 阻燃/额定火焰 通过 ROHS 认证 Flame Retardant 脱模剂 优良的脱模剂 PRL PC-HM-FR1-(color)-1 is a Polycarbonate (PC) product filled with 10% glass fiber. It can be processed by injection molding and is available in North America. Characteristics include: Flame Rated RoHS Compliant Flame Retardant Good Mold Release Mold Release Agent |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.26 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
5.0 to 12 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
TD:3.2 mm TD:3.2 mm |
0.20 to 0.50 | % | ASTM D955 |
MD:3.2 mm MD:3.2 mm |
0.20 to 0.50 | % | ASTM D955 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃,3.2mm 23℃,3.2mm |
110 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 2 | |
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
UL 746 | ||
3.0 mm 3.0 mm |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
UL 746 | ||
1.5 mm 1.5 mm |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
UL 746 | ||
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
相比漏电起痕指数 Compared to the leakage tracing index |
|||
1.50 mm 1.50 mm |
UL 746 | ||
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
UL 746 | ||
1.5 mm 1.5 mm |
UL 746 | ||
热丝引燃 Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
1.5 mm 1.5 mm |
UL 746 | ||
3.0 mm 3.0 mm |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.50 mm,所有颜色 1.50 mm, all colors |
UL 94 | ||
3.00 mm,所有颜色 3.00 mm, all colors |
UL 94 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
断裂,3.18 mm Fracture, 3.18 mm |
MPa | ASTM D638 | |
屈服,3.17 mm Yield, 3.17 mm |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂,3.18 mm Fracture, 3.18 mm |
% | ASTM D638 | |
屈服,3.18 mm Yield, 3.18 mm |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
3.17 mm 3.17 mm |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
3.18 mm 3.18 mm |
MPa | ASTM D790 | |
洛氏硬度 Rockwell hardness |
ASTM D785 | ||
M 级 M-level |
ASTM D785 | ||
R 级 R-level |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 标准 B (120°C/h), 载荷2 (50N) |
【新闻资讯】查看全部
2015年塑料制品产量7560.8万吨 同比增长0.95%
2016-01-27 中国轻工业经济运行及预测预警系统监测显示:2015年1-12月份,塑料制品行业规模遇上企业完成塑料制品产量7560.8万吨,同比增长0.95%。其中:12月份完成产量739.77万吨,同比增长4.96%。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |