牌号简介 About |
---|
Bayflex 190是一种ELPO(可电泳)高性能聚脲,具有优异的热稳定性、低吸湿性、低热膨胀特性和优异的抗冲击性。用这种材料制成的零件具有优异的表面和油漆粘合质量,并且具有与涂漆钢零件相当的DOI(图像区别)。Bayflex 190系统是卡车挡泥板和尾门等应用的最佳选择。与任何产品一样,在给定应用中使用Bayflex 190系统必须由用户提前进行测试(包括现场测试等),以确定适用性。Bayflex 190是一种配制的轮辋系统,作为两种液体成分提供。A组分为二苯基甲烷二异氰酸酯(MDI)预聚物,B组分为聚醚胺体系。 Bayflex 190 is an ELPO (electrophoresis-capable) high-performance polyurea with excellent heat stability, low moisture absorption, low thermal expansion characteristics, and excellent impact resistance. Parts made from this material have superior surface and paint adhesion qualities and have a DOI (Distinction of Image) comparable to painted steel parts. The Bayflex 190 system is an excellent choice for applications such as truck fenders and tailgates. As with any product, use of the Bayflex 190 system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability. Bayflex 190 is a formulated RIM system, supplied as two liquid components. Component A is a diphenylmethane diisocyanate (MDI) prepolymer and Component B is a polyether amine system. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.25 | g/cm³ | ASTM D792, ASTM D1622 |
收缩率 Shrinkage rate |
|||
MD MD |
0.43 | % | 内部方法 |
吸水率 Water absorption rate |
|||
40hr,3.81 mm 40hr,3.81 mm |
0.10 | % | 内部方法 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
弯曲模量 Bending modulus |
ASTM D790 | ||
-30℃,3.81 mm -30℃,3.81 mm |
2760 | MPa | |
23℃,3.81 mm 23℃,3.81 mm |
1720 | MPa | |
65℃,3.81 mm 65℃,3.81 mm |
MPa | ||
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
断裂,3.81 mm Fracture, 3.81 mm |
MPa | ASTM D638 | |
断裂,3.81 mm Fracture, 3.81 mm |
MPa | ASTM D412 | |
拉伸应变 Tensile strain |
|||
断裂,3.81 mm Fracture, 3.81 mm |
% | ASTM D638 | |
断裂,3.81 mm Fracture, 3.81 mm |
% | ASTM D412 | |
撕裂强度 tear strength 1 |
|||
3.81 mm 3.81 mm 1 |
kN/m | ASTM D624 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
落锤冲击 Drop hammer impact 3 |
|||
3.81 mm 3.81 mm 3 |
J/m | 内部方法 | |
Heat Sag - 6 in Overhang Heat Sag - 6 in Overhang 4 |
ASTM D3769 | ||
191℃,3.81 mm 191℃,3.81 mm |
mm | ||
250℃,3.81 mm 250℃,3.81 mm |
mm | ||
memo_intro memo_intro |
|||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:3.81 mm MD:3.81 mm |
1/℃ | ASTM D696 | |
热固组件 Thermosetting components 2 |
|||
部件 A Component A |
|||
部件 B Component B |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 C 模具 |
3 105 Index |
4 5 mph |
5 1 hr |