牌号简介 About |
---|
19N930是一种低密度聚乙烯,用于注塑成型。它是一种中等mfr材料,具有良好的流动性能和允许短周期时间。该模制品具有内应力低、刚度好、翘曲度低、光泽度高的特点。应用:19N930是推荐的注射成型柔性产品,要求良好的流动性能和短周期时间。这种材料特别适用于瓶盖、瓶盖、家居用品和玩具等产品。 19N930 is a low-density polyethylene intended for injection molding. It is a medium MFR material, having good flow properties and allowing short cycle time. The moulded article is characterized by low degree of built-in stress, good stiffness, low warpage and high gloss. Applications: 19N930 is recommended for injection moulding of flexible products which require good flow properties and short cycle time. The material is especially suitable for products like caps and closures, household goods and toys. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density 3 |
0.920 | g/cm³ | ISO 1183/D |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,0.325kg 190℃,0.325kg |
7.5 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,模压成型 Shaw's D, molded |
47 | ISO 868 | |
拉伸强度 tensile strength |
|||
断裂,模压成型 Fracture, molded |
10.0 | MPa | ISO 527-2 |
屈服,模压成型 Yield, molding |
9.00 | MPa | ISO 527-2 |
拉伸应变 Tensile strain |
|||
断裂,模压成型 Fracture, molded |
% | ISO 527-2 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-20℃ -20℃ |
kJ/m² | ISO 180 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
熔融温度 Melting temperature |
℃ | DSC |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Conditioned according to ISO 1872/1 |