牌号简介 About |
---|
DuraGrip 6150BK是一种特殊用途的熔融加工弹性体(MPE),易于用于注塑和挤压工艺。DGR 6150BK具有极佳的柔软触感,可与尼龙、ABS、PC、PC/ABS粘合。DuraGrip 6100系列具有吸湿性,使用前需要干燥。 DuraGrip® 6150BK is designed to be a special purpose Melt Processible Elastomer (MPE) that is easy to use in injection molding and extrusion processes. DGR 6150BK has an excellent soft touch feel and will Bond to Nylon, ABS, PC, PC/ABS. DuraGrip® 6100 series is hygroscopic and requires drying prior to use. |
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A,5 秒 Shore A, 5 seconds |
52 | ISO 868 | |
邵氏 A,5 秒 Shore A, 5 seconds |
52 | ASTM D2240 | |
泰伯耐磨性 Taber abraser |
|||
1000 周期,1.0E+6 g,CS-17 转轮 1000 cycles, 1.0E+6 g, CS-17 wheel |
144 | mg | ASTM D1044 |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸永久变形 Tensile permanent deformation |
|||
100% 应变 100% strain |
3 | % | ASTM D412 |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
5.86 | MPa | ISO 37 |
屈服,23℃ Yield, 23 ℃ |
MPa | ASTM D412 | |
100% 应变,23℃ 100% strain, 23 ℃ |
MPa | ISO 37 | |
100% 应变 100% strain |
MPa | ASTM D412 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 37 | |
断裂 fracture |
% | ASTM D412 | |
撕裂强度 tear strength |
|||
24℃ 24℃ |
kN/m | ASTM D624 | |
压缩形变 Compression deformation |
ASTM D395B | ||
24℃,22 hr 24℃,22 hr |
% | ASTM D395B | |
70℃,22 hr 70℃,22 hr |
% | ASTM D395B | |
100℃,22 hr 100℃,22 hr |
% | ASTM D395B | |
压缩形变 Compression deformation |
ISO 815 | ||
24℃,22 hr 24℃,22 hr |
% | ISO 815 | |
70℃,22 hr 70℃,22 hr |
% | ISO 815 | |
100℃,22 hr 100℃,22 hr |
% | ISO 815 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
脆化温度 Embrittlement temperature |
℃ | ISO 812 | |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 The rate of change in tensile strength in air |
ASTM D573 | ||
70℃,168 hr 70℃,168 hr |
% | ASTM D573 | |
100% Strain,70℃,168 hr 100% Strain,70℃,168 hr |
% | ASTM D573 | |
100℃,168 hr 100℃,168 hr |
% | ASTM D573 | |
100% Strain,100℃,168 hr 100% Strain,100℃,168 hr |
% | ASTM D573 | |
空气中拉伸强度的变化率 The rate of change in tensile strength in air |
ISO 188 | ||
70℃,168 hr 70℃,168 hr |
% | ISO 188 | |
100% Strain 70℃,168 hr 100% Strain 70℃,168 hr |
% | ISO 188 | |
100℃,168 hr 100℃,168 hr |
% | ISO 188 | |
100% Strain 100℃,168 hr 100% Strain 100℃,168 hr |
% | ISO 188 | |
空气中极限伸长率的变化率 The rate of change in ultimate elongation in air |
ASTM D573 | ||
70℃,168 hr 70℃,168 hr |
% | ASTM D573 | |
100℃,168 hr 100℃,168 hr |
% | ASTM D573 | |
断裂时拉伸应力变化 Changes in tensile stress during fracture |
ISO 1817 | ||
70℃,168 hr 70℃,168 hr |
% | ISO 1817 | |
100℃,168 hr 100℃,168 hr |
% | ISO 1817 | |
体积变化 Volume change |
ASTM D471 | ||
24℃,168 hr,in Reference Fuel B 24℃,168 hr,in Reference Fuel B |
% | ASTM D471 | |
70℃,168 hr,in ASTM #1 Oil 70℃,168 hr,in ASTM #1 Oil |
% | ASTM D471 | |
70℃,168 hr,in IRM 903 Oil 70℃,168 hr,in IRM 903 Oil |
% | ASTM D471 | |
70℃,168 hr,in Water 70℃,168 hr,in Water |
% | ASTM D471 | |
体积变化 Volume change |
ISO 1817 | ||
24℃,168 hr,in Reference Fuel B 24℃,168 hr,in Reference Fuel B |
% | ISO 1817 | |
70℃,168 hr,in ASTM #1 Oil 70℃,168 hr,in ASTM #1 Oil |
% | ISO 1817 | |
70℃,168 hr,in IRM 903 Oil 70℃,168 hr,in IRM 903 Oil |
% | ISO 1817 | |
70℃,168 hr,in Water 70℃,168 hr,in Water |
% | ISO 1817 | |
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ASTM D792 | |
密度 Density |
g/cm³ | ISO 1183 | |
收缩率 Shrinkage rate |
|||
MD:1.59 mm MD:1.59 mm |
% | ASTM D955 | |
MD:3.2 mm MD:3.2 mm |
% | ASTM D955 | |
TD:1.59 mm TD:1.59 mm |
% | ASTM D955 | |
TD:3.2 mm TD:3.2 mm |
% | ASTM D955 | |
收缩率 Shrinkage rate |
|||
TD:1.59 mm TD:1.59 mm |
% | ISO 294-4 | |
MD:1.59 mm MD:1.59 mm |
% | ISO 294-4 | |
TD:3.2 mm TD:3.2 mm |
% | ISO 294-4 | |
MD:3.2 mm MD:3.2 mm |
% | ISO 294-4 | |
熔体表观粘度 Apparent viscosity of melt |
|||
190℃,300 sec^-1 190℃,300 sec^-1 |
Pa·s | ASTM D3835 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 C 模具 |
【新闻资讯】查看全部
合成革的功用化开展
2015-11-25 合成革正向功能化高端市场发展。产品品种繁多,应用领域细分,户要求更全面,应用性能更突出,是目前市场对合成革企业的要求,和产品发展趋势。 合成革是高分子材料的重要分支,她的发展方向同样遵循这高分子材料功能化的发展方向。主要功能化包括:负离子、杀菌、导电(屏蔽、生热)、消音阻尼减震、导热、隔热、阻火、磁性、隐身、红外保健、热致变色和电致变色、形状记忆、呼吸功能等等。 负离子合成革 研究开发新型功能化合成革。其面层 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |