牌号简介 About |
---|
HR-242U是一种以己烷为共聚单体的经认证的一级共聚物树脂,具有紫外线(UV)添加剂;设计用于旋转成型,特殊的大型罐应用。HR-242U是紫外线稳定的,有35目粉末。 HR-242U is a certified prime grade copolymer resin using hexane as comonomer, with Ultraviolet (UV) additiv; designed for rotational molding, special large tank applications. HR-242U is UV stabilized and is available in 35 mesh powder. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.942 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
2.0 | g/10min | ASTM D1238 |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
100%非离子洗涤剂,F50 100% non-ionic detergent, F50 |
780 | hr | ASTM D1693A |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 2 |
|||
屈服 yield 2 |
24.0 | MPa | ASTM D638 |
拉伸应变 Tensile strain 2 |
|||
屈服 yield 2 |
11 | % | ASTM D638 |
弯曲模量 Bending modulus 3 |
|||
1% 正割 1% secant 3 |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-40℃,45.7 mm -40℃,45.7 mm |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 0.051 in/min |
【新闻资讯】查看全部
聚氨酯泡沫塑料将取得全面开展
2017-11-22 随着泡沫体生产的逐渐成熟,市场供应的不断扩大,虽然聚酯型软质泡沫塑料性能优良,但由于成本较高,价格较贵,不适合某些商品要求,因此促使了需要寻找比聚酯价廉的树脂来取代它。 在纷纷进行研究后,美国杜邦公司首先用聚四亚甲基醚二元醇来代替聚酯制造软质泡沫塑料,这种泡沫体柔软,回弹性好,耐水解性优良,其价格接近于聚酯的价格。 后来改用了以廉价的氧化烯烃、蓖麻油等为原料制备的聚醚树脂用于软质聚氨酯泡沫塑料的生产。用这种聚醚制得的制品,性能较好,价格较低,使聚氨酯工业又发 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |