牌号简介 About |
---|
Daplen™ EE168AI是一种10%矿物填充聚丙烯化合物,用于注塑成型。这种材料在冲击强度和刚度之间具有极好的平衡,并且易于加工。 Daplen EE168AI is a 10% mineral filled polypropylene compound intended for injection moulding. This material has an excellent balance between impact strength and stiffness and is easy to process. Applications Daplen EE168AI has been developed especially for the car industry to be used in automotive interior parts. Dashboards Door panels and pockets Pillar trims Automotive interior applications Special Features High scratch resistance - Low gloss High dimensional stability |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.990 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
14 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
1.1 | % | 内部方法 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
注塑成型 injection molding |
1700 | MPa | ISO 527-1-2 |
拉伸强度 tensile strength |
|||
屈服,注塑成型 Yield, injection molding |
20.0 | MPa | ISO 527-2/50 |
拉伸应变 Tensile strain |
|||
屈服,注塑成型 Yield, injection molding |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus 2 |
|||
注塑成型 injection molding 2 |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
注塑成型 injection molding |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-20℃,注塑成型 -20 ℃, injection molding |
kJ/m² | ISO 179/1eA | |
23℃,注塑成型 23 ℃, injection molding |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-20℃,注塑成型 -20 ℃, injection molding |
kJ/m² | ISO 179/1eU | |
23℃,注塑成型 23 ℃, injection molding |
ISO 179/1eU | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/1A | ||
-20℃,注塑成型 -20 ℃, injection molding |
kJ/m² | ISO 180-1A | |
23℃,注塑成型 23 ℃, injection molding |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
ISO 180/1U | ||
-20℃,注塑成型 -20 ℃, injection molding |
kJ/m² | ISO 180/1U | |
23℃,注塑成型 23 ℃, injection molding |
ISO 180/1U | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
B50 B50 |
℃ | ISO 306 | |
Melt Energy Melt Energy |
kJ/kg | ISO 11357 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
雾化 atomization |
|||
16 hr,100℃ 16 hr,100℃ |
g | DIN 75201 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
排放 discharge |
µgC/g | VDA 277 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.079 in/min |
【新闻资讯】查看全部
国际能源署预计全球化石燃料总需求从2050年下降
2021-10-15 搜料网资讯: 国际能源署13日在巴黎发布《2021年世界能源展望》报告预测,根据各国现行及已宣布政策标准,世界对化石燃料的总需求将在本世纪30年代达到峰值并趋于平稳,从2050年开 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |