牌号简介 About |
---|
该树脂是一种热稳定、冲击改性的6型接枝共聚物,开发用于注塑和挤出应用,需要提高干模韧性和灵活性。它也可以在非热稳定(超中8253)和/或色素版本。应用Ultramid® 8253 HS通常推荐用于插头、插座、柔性连接器盖、除草机部件、夹子、紧固件、法兰、键外壳以及许多柔性管应用。 This resin is a heat stabilized, impact modified type 6 graft copolymer developed for both injection molding and extrusion applications requiring improved dry as molded toughness and increased flexibility. It is also available in non-heat stabilized (Ultramid 8253) and/or pigmented versions. Applications Ultramid 8253 HS is generally recommended for applications such as plugs, receptacles, flexible connector covers, weed trimmer components, clips, fasteners, flanges, key housings as well as many flexible tubing applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.09 | g/cm³ | ASTM D792 |
密度 Density |
1.09 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
1.2 | % | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
8.1 | % | ISO 62 |
饱和 saturated |
8.1 | % | ASTM D570 |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
平衡,50% RH Balance, 50% RH |
% | ASTM D570 | |
24hr 24hr |
% | ASTM D570 | |
23℃,24hr 23℃,24hr |
% | ISO 62 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179 | ||
-30℃ -30℃ |
kJ/m² | ISO 179 | |
23℃ 23℃ |
kJ/m² | ISO 179 | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
ISO 179 | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-40℃ -40℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
落下冲击阻力 Falling impact resistance |
|||
23℃ 23℃ |
J | Internal Method | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | ISO 3146 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD TD |
1/℃ | ||
MD MD |
1/℃ | ||
MD MD |
1/℃ | ASTM E831 | |
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
UL 746 | ||
0.71 mm 0.71 mm |
℃ | UL 746 | |
0.75 mm 0.75 mm |
℃ | UL 746 | |
6.0 mm 6.0 mm |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
UL 746 | ||
0.71 mm 0.71 mm |
℃ | UL 746 | |
0.75 mm 0.75 mm |
℃ | UL 746 | |
1.5 mm 1.5 mm |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
UL 746 | ||
3.0 mm 3.0 mm |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
1.50 mm 1.50 mm |
ohms·cm | ASTM D257 | |
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.75 mm 0.75 mm |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
6.00 mm 6.00 mm |
UL 94 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
ISO 527-2 | ||
-40℃ -40℃ |
MPa | ISO 527-2 | |
23℃ 23℃ |
MPa | ISO 527-2 | |
80℃ 80℃ |
MPa | ISO 527-2 | |
120℃ 120℃ |
MPa | ISO 527-2 | |
150℃ 150℃ |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
ISO 527-2 | ||
屈服,-40℃ Yield, -40 ℃ |
MPa | ISO 527-2 | |
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2 | |
屈服,80℃ Yield, 80 ℃ |
MPa | ISO 527-2 | |
屈服,120℃ Yield, 120 ℃ |
MPa | ISO 527-2 | |
屈服,150℃ Yield, 150 ℃ |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
ASTM D638 | ||
断裂,-40℃ Fracture, -40 ℃ |
MPa | ASTM D638 | |
断裂,23℃ Fracture, 23 ℃ |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
ASTM D638 | ||
屈服,23℃ Yield, 23 ℃ |
% | ISO 527-2 | |
屈服,-40℃ Yield, -40 ℃ |
% | ASTM D638 | |
屈服,23℃ Yield, 23 ℃ |
% | ASTM D638 | |
屈服,80℃ Yield, 80 ℃ |
% | ASTM D638 | |
屈服,121℃ Yield, 121 ℃ |
% | ASTM D638 | |
标称拉伸断裂应变 Nominal tensile fracture strain |
ISO 527-2 | ||
-40℃ -40℃ |
% | ISO 527-2 | |
23℃ 23℃ |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
ASTM D790 | ||
23℃ 23℃ |
MPa | ISO 178 | |
-40℃ -40℃ |
MPa | ASTM D790 | |
23℃ 23℃ |
MPa | ASTM D790 | |
65℃ 65℃ |
MPa | ASTM D790 | |
90℃ 90℃ |
MPa | ASTM D790 | |
121℃ 121℃ |
MPa | ASTM D790 | |
弯曲强度 bending strength |
ASTM D790 | ||
23℃ 23℃ |
MPa | ISO 178 | |
-40℃ -40℃ |
MPa | ASTM D790 | |
23℃ 23℃ |
MPa | ASTM D790 | |
65℃ 65℃ |
MPa | ASTM D790 | |
90℃ 90℃ |
MPa | ASTM D790 | |
121℃ 121℃ |
MPa | ASTM D790 | |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
特殊值 Special value |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
屈服,-40℃ Yield, -40 ℃ |
MPa | ASTM D638 | |
屈服,23℃ Yield, 23 ℃ |
MPa | ASTM D638 | |
屈服,80℃ Yield, 80 ℃ |
MPa | ASTM D638 | |
屈服,121℃ Yield, 121 ℃ |
MPa | ASTM D638 | |
断裂,-40℃ Fracture, -40 ℃ |
% | ASTM D638 | |
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D638 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
陕西石化联合会调研企业减煤降碳
2021-09-04 搜料网资讯: 8月23日至29日为全国节能宣传周。连日来,陕西省石油和化学工业联合会技术委员会主任胡海峰一行,先后走访蒲城清洁能源化工有限责任公司、陕西渭河煤化工集团有限 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |