牌号简介 About |
---|
TC-816 A/B是一种耐用的填充聚氨酯系统,具有优异的复制性能。TC-816 A/B具有低收缩、低温和快速拆卸的特点。产品亮点:特别低的粘度在半凝胶阶段可作为浆料,如果需要的话,低收缩率有助于低收缩,将很容易结合到自身,更大的沉降阻力与环氧表面涂层很好地结合在可擦拭工具上,安全地与铂基硅酮一起使用。 TC-816 A/B is a durable, filled polyurethane system that offers excellent duplication properties. TC-816 A/B exhibits low shrink, low exotherm and quick demold times. Product Highlights: Exceptionally low viscosity Workable in semi-gel stage as a paste if desired Low exotherm contributing to low shrinkage Will readily bond to itself Greater settling resistance Integrates well with epoxy surface coats for polishable tools Safe to use with platinum based silicones |
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
83 到 87 | ASTM D2240 | |
压缩强度 compressive strength |
63.4 | MPa | ASTM D695 |
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.62 | g/cm³ | ASTM D792 |
密度 Density |
|||
Part A:25℃ Part A:25℃ |
1.596 | g/cm³ | |
Part B:25℃ Part B:25℃ |
1.596 | g/cm³ | |
收缩率 Shrinkage rate |
% | ASTM D2566 | |
布络克菲尔德粘度 Brookfield viscosity |
|||
混合,25℃ Mixing, 25 ℃ |
Pa·s | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
热固组件 Thermosetting components |
|||
部件 A Component A |
|||
部件 B Component B |
|||
贮藏期限 Storage period |
wk | ||
脱模时间 stripping time 2 |
|||
25℃ 25℃ 2 |
min | ||
工作时间 working hours 3 |
|||
25℃ 25℃ 3 |
min |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 mass dependent |
3 1-lb. mass |
【新闻资讯】查看全部
东方盛虹2020年利润3.16亿元 Q1净利回暖超5亿元
2021-04-18 搜料网资讯: 4月14日晚间, 东方 盛虹披露了2020年业绩报告及2021年一季度业绩预告称。2020年公司实现营业收入227.77亿元,同比降低8.48%;归母净利润3.16亿元,同比下降80.40%,拟10派1元 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |