牌号简介 About |
---|
优点和特点Eltex® PF6220KJ是一种含有己烯-1作为共聚单体的聚乙烯共聚物,由茂金属催化剂制备。它具有以下特性:高冲击强度和刚度优良的光学特性非常好的气泡稳定性和挤出性,类似于最佳LLDPE吹塑薄膜等级低温密封特性Eltex® PF6220KJ,具有高滑膜和易开启特性。添加其他聚合物、母粒和颜料可能会改变薄膜的滑动和抗阻塞性能。应用程序Eltex® PF6220KJ已开发用于整理收缩包装、食品包装和其他薄膜应用,在这些应用中,薄膜强度和刚度之间需要良好的平衡以及良好的光学性能。此外,ELTEX PF6220KJ还具有易挤压性。 Benefits & Features Eltex® PF6220KJ is a polyethylene copolymer containing hexene-1 as the comonomer produced with a metallocene catalyst. It offers the following properties: High impact strength and rigidity Excellent optical properties Very good bubble stability and extrudability similar to the best LLDPE blown film grades Low temperature sealing characteristics Eltex® PF6220KJ offers high slip film with easy opening properties. Addition of other polymers, masterbatch and pigments may alter film slip and antiblock performance. Applications Eltex® PF6220KJ has been developed for use in collation shrinkwrap, food packaging and other thin film applications where an excellent balance between film strength and rigidity is required together with good optical properties. In addition, Eltex ® PF6220KJ offers easy extrudability. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.920 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
2.1 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
|||
吹塑薄膜 Blown film |
< 0.25 | ASTM D1894 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
25 | µm | |
拉伸模量 Tensile modulus |
ISO 527-3 | ||
1% 正割,MD,25 µm,吹塑薄膜 1% secant, MD, 25 µ m, blow molded film |
160 | MPa | ISO 527-3 |
1% 正割,TD,25 µm,吹塑薄膜 1% secant, TD, 25 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,屈服,25 µm,吹塑薄膜 MD, yield, 25 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,屈服,25 µm,吹塑薄膜 TD, yield, 25 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸应变 Tensile strain |
ISO 527-3 | ||
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
% | ISO 527-3 | |
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
% | ISO 527-3 | |
落锤冲击 Drop hammer impact |
|||
25 µm,吹塑薄膜 25 µ m, blow molded film |
g | ASTM D1709-A | |
撕裂强度 tear strength |
|||
TD,25 µm,吹塑薄膜 TD, 25 µ m, blow molded film |
g | ASTM D1922 | |
MD,25 µm,吹塑薄膜 MD, 25 µ m, blow molded film |
g | ASTM D1922 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融峰值温度 Melting peak temperature 3 |
℃ | ASTM D3418 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,25 µm,吹塑薄膜 45 °, 25 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
25 µm,吹塑薄膜 25 µ m, blow molded film |
% | ASTM D1003 |
备注 |
---|
1 Silica |
2 一般属性:这些不能被视为规格。 |
3 2nd heating |
【新闻资讯】查看全部
华东塑价一片绿!PE个别牌号暴跌900,PP跌额在20-200区间!(20220524)
2022-05-24 今日华东地区塑料市场价一片飘绿!PE大部分下跌,普遍跌额在50-250区间,个别牌号暴跌800-900;PP市场价全线下挫,跌额在20-200区间,下挫幅度不大。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |