Moplen EP310DC是一种低流动性异相共聚物,设计用于挤出应用,在挤出应用中,平滑的可加工性和高机械性能至关重要。主要应用是用于重型应用的薄膜挤压、胶带、层压薄膜和用于清洁剂等的挤压吹塑成型容器。Moplen EP310DC适用于食品接触。有关监管信息,请参阅Moplen EP310DC产品管理公告(PSB)。 Moplen EP310DC is a low fluidity polypropylene heterophasic copolymer. It does not contain anti-blocking and slip additives. Moplen EP310DC is typically used by customers for extrusion applications when high mechanical properties are of the utmost importance. It is normally extruded by customers in single layer film for lamination on other substrates, obtaining structures that can be processed under high retorting conditions. This grade has been reported to be used in some other typical applications, such as extruded film for adhesive tapes, lamination film, freezer film, pipes, fittings and containers produced by extrusion blow molding. Customers also reported that can be used as a building block for heavy duty bags, delivering high impact and thermal resistance over a broad range of temperatures. Moplen EP310DC has been reported by customers to exhibit high impact, good puncture, good tear resistance, high seal strength and seal integrity. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.900 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
0.80 | g/10min | ISO 1133 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
割线模量 Secant modulus 2 |
|||
MD,60 µm MD,60 µm 2 |
1200 | MPa | ASTM D882 |
拉伸强度 tensile strength 3 |
ASTM D882 | ||
MD,屈服,60 µm MD, yield, 60 µ m |
27.0 | MPa | ASTM D882 |
MD,断裂,60 µm MD, fracture, 60 µ m |
49.0 | MPa | ASTM D882 |
拉伸应变 Tensile strain 3 |
ASTM D882 | ||
MD,屈服,60 µm MD, yield, 60 µ m |
% | ASTM D882 | |
MD,断裂,60 µm MD, fracture, 60 µ m |
% | ASTM D882 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-20℃ -20℃ |
kJ/m² | ISO 179/1eA | |
0℃ 0℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
60.0 µm 60.0 µm |
ASTM D2457 | ||
雾度 Haze |
|||
60 µm 60 µm |
% | ASTM D1003 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ISO 868 | ||
拉伸模量 Tensile modulus |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
ISO 527-2 | ||
屈服 yield |
% | ISO 527-2 | |
断裂 fracture |
% | ISO 527-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.98 in/min |
3 20 in/min |
【新闻资讯】查看全部
美利肯发布年度可持续发展报告
2022-05-23 近日,美利肯公司发布了第四份年度可持续发展报告,这份报告是公司在实现其2025年可持续发展目标过程中的一个重要组成部分。 美利肯公司的第四份报告按照全球报告倡议组织(GRI |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |