牌号简介 About |
---|
Clearflex H&T FGH B3是一种线性低密度聚乙烯,由专有增强Z-N催化剂制成,适用于吹塑薄膜技术。该树脂含有抗氧化剂、助滑剂和防堵剂,具有极低的密度和高分子量的特点。与标准Clearflex VLDPE等级相比,Clearflex H&T FGH B3具有较低的密封起始温度、优异的光学性能和机械性能。主要应用Clearflex H&T FGH B3被推荐用于生产要求光学性能、耐穿刺性、冲击强度和良好密封性相结合的吹塑薄膜。Clearflex H&T FGH B3也推荐用于层压膜的生产。 Clearflex H&T FGH B3 is a linear low density polyethylene, made by proprietary enhanced Z-N catalyst, suitable for blown film technology. The resin, containing antioxidants slip agent and antiblock, is characterized by a very low density and high molecular weight. Compared to std Clearflex VLDPE grades, Clearflex H&T FGH B3 offers lower seal initiation temperature, excellent optical properties and mechanical performances. Main Applications Clearflex H&T FGH B3 is recommended to produce blown film requiring a combination of optical properties, puncture resistance and impact strength and very good sealability. Clearflex H&T FGH B3 is also recommended in the production of Lamination film. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.911 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.90 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
摩擦系数 friction coefficient |
|||
动态,吹塑薄膜 Dynamic, blow molded film |
> 0.50 | ISO 8295 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
10 to 50 µm | ||
拉伸模量 Tensile modulus |
ISO 527-3 | ||
1% 正割,MD,吹塑薄膜 1% secant, MD, blow molded film |
140 | MPa | ISO 527-3 |
1% 正割,TD,吹塑薄膜 1% secant, TD, blow molded film |
MPa | ISO 527-3 | |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,屈服,吹塑薄膜 MD, yield, blow molded film |
MPa | ISO 527-3 | |
TD,屈服,吹塑薄膜 TD, yield, blow molded film |
MPa | ISO 527-3 | |
MD,断裂,吹塑薄膜 MD, fracture, blow molded film |
MPa | ISO 527-3 | |
TD,断裂,吹塑薄膜 TD, fracture, blow molded film |
MPa | ISO 527-3 | |
拉伸应变 Tensile strain |
ISO 527-3 | ||
MD,断裂,吹塑薄膜 MD, fracture, blow molded film |
% | ISO 527-3 | |
TD,断裂,吹塑薄膜 TD, fracture, blow molded film |
% | ISO 527-3 | |
落锤冲击 Drop hammer impact |
|||
吹塑薄膜 Blown film |
g | ISO 7765-1/A | |
撕裂强度 tear strength 2 |
ISO 6383-2 | ||
MD MD |
kN/m | ISO 6383-2 | |
TD TD |
kN/m | ISO 6383-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
熔融温度 Melting temperature |
℃ | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,吹塑薄膜 45 °, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
吹塑薄膜 Blown film |
% | ISO 14782 |
备注 |
---|
2 Blown Film |
【新闻资讯】查看全部
KUKA机器人中国二期厂房奠基典礼盛大举行
2017-01-12 全球领先的工业机器人制造商KUKA公司隆重举行中国二期厂房奠基仪式,宣布再次加大对中国的投资,以期更好地满足中国市场对工业自动化的需求。KUKA公司以引领世界工业机器人技术发展潮流的先进产品及技术,履行对中国市场的长期承诺,为工业客户提供优秀的智能产品及解决方案。 KUKA公司自2000年进入中国市场,至今已有16年坚实的发展历史,并凭借在生产自动化和机器人领域110多年的专业知识和丰富经验,不断拓展在中国的业务范围。KUKA机器人中国一期厂房于2013年顺利投产,3年内即 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |