牌号简介 About |
---|
HIVOREX 5220B采用泥浆工艺技术生产。这种树脂非常适合用于吹塑应用。HIVOREX 5220B旨在提供高刚度、优异的抗冲击性、良好的表面、抗静电性。 HIVOREX 5220B is produced by slurry process technology. This resin is ideally suited for use in blow molding application. HIVOREX 5220B is designed to offer high stiffness, excellent impact resistance, good surface, anti-static. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.959 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.40 | g/10min | ASTM D1238 |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
F50 F50 |
60.0 | hr | ASTM D1693 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服 yield |
27.5 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
> 500 | % | ASTM D638 |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
稀土转光膜为作物提质增产
2018-07-11 山东淄博舜明荧光科技有限公司采用有机/无机稀土转光粉制成的稀土转光膜,可将瓜果等作物的光合速率提高 20%以上,平均产量提高20%~30%。 目前的农用塑料棚膜大多具有耐老化、无滴、防雾和保温功能,但这些功能只是被动利用太阳能,不能通过调节太阳能波长主动利用太阳能。舜明公司将稀土材料通过聚合低成本制成稀土转光粉,掺入农膜后制成稀土转光膜,为全面升级棚膜提供了基础。 该稀土转光膜可将太阳光中有害的紫外光和无效绿光转换为有利于植物生长的蓝光和红光, 促进作物对营 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |