牌号简介 About |
---|
LLBF-120J是一种具有丁烯共聚单体的经认证的底漆树脂,设计用于生产通用包装用吹塑薄膜。LLBF-120J具有加工性好、薄膜强度好、热封温度范围宽等优点。LLBF-120J的应用包括服装袋,生产袋和衬里。LLBF-120J不打滑,抗阻能力强。LLBF-120J符合FDA法规21CFR 177.1520(c)3.1a和大多数有关在食品接触中使用聚乙烯的国际法规。 LLBF-120J is a certified prime resin with Butene-comonomer, designed for production of Blown films used in general purpose packaging. LLBF-120J features excellent combination of easy processability with good film strength as well as wide heat sealing temperature range. LLBF-120J applications include garment bags, produce bags and liners. LLBF-120J contains no slip and high antiblock. LLBF-120J complies with FDA regulation 21CFR 177.1520(c)3.1a and with most international regulations concerning the use of Polyethylene in contact with food articles. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.920 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.0 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
25 | µm | |
割线模量 Secant modulus |
ASTM D882 | ||
1% 正割,MD:25 µm 1% secant, MD: 25 µ m |
193 | MPa | ASTM D882 |
1% 正割,TD:25 µm 1% secant, TD: 25 µ m |
223 | MPa | ASTM D882 |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服,25 µm MD, yield, 25 µ m |
MPa | ASTM D882 | |
TD,屈服,25 µm TD, yield, 25 µ m |
MPa | ASTM D882 | |
MD,断裂,25 µm MD, fracture, 25 µ m |
MPa | ASTM D882 | |
TD,断裂,25 µm TD, fracture, 25 µ m |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,25 µm MD, fracture, 25 µ m |
% | ASTM D882 | |
TD,断裂,25 µm TD, fracture, 25 µ m |
% | ASTM D882 | |
落锤冲击 Drop hammer impact 1 |
|||
25 µm 25 µm 1 |
g | ASTM D1709-A | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD:25 µm MD:25 µm |
g | ASTM D1922 | |
TD:25 µm TD:25 µm |
g | ASTM D1922 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,25.4 µm,吹塑薄膜 45 °, 25.4 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
25.4 µm,吹塑薄膜 25.4 µ m, blow molded film |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 F50 |
【新闻资讯】查看全部
七院工艺设计院研发国际首条酚醛树脂自动化消费线
2016-08-01 日前,中国航天科工七院工艺设计院研发的国内首条酚醛树脂自动化生产线已经在北京玻璃钢研究院投入使用,创新工作取得突破。 北京玻璃钢研究院是我国玻璃钢/复合材料行业最大的综合性应用研究开发机构,其研发制造的高品质复合材料广泛应用于航空航天、交通运输、电子电力等领域,是国内唯一为军工产品研制提供树脂材料的认证单位。 由于酚醛树脂生产线技术难点多,工艺复杂,目前国内没有自主研发的自动化生产线,现有的酚醛树脂生产线均从美国、英国、日本等国进口,集中在民品领域,产品质量 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |