牌号简介 About |
---|
60GF5是一种25%玻璃纤维增强尼龙6,具有良好的机械性能,适用于一般用途的注塑应用。 60GF5 is a 25% glass fibre reinforced nylon 6 that offers good mechanical performance and is suitable for general purpose injection moulding applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.25 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
0.70 到 1.2 | % | 内部方法 |
吸水率 Water absorption rate |
|||
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
2.3 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
7000 | MPa | ISO 527-2 |
拉伸强度 tensile strength |
125 | MPa | ISO 527-2 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
kJ/m² | ISO 179-1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
kJ/m² | ISO 179/1eU | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
kJ/m² | ISO 180/A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
|||
3 mm 3 mm |
kV/mm | IEC 60243-1 | |
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
1.50 mm,Teknor Apex测试结果 1.50 mm, Teknor Apex test results |
UL 94 | ||
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Mould shrinkage is significantly influenced by many factors including wall thickness, gating, moulding shape and processing conditions. The range values given are determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding). |
【新闻资讯】查看全部
法网恢恢 塑料黑窝点被端
2017-09-28 日前,涿州市公安局环境安全保卫大队经工作打掉一个非法加工塑料颗粒的黑窝点,抓获违法行为人邓某(男、27岁,雄县人) 9月8日,涿州市公安局环境安全保卫大队接到报警后,火速出击,成功捣毁一非法加工塑料颗粒的黑窝点。 经查:自2014年至案发,在涿州市义和庄某村村东,违法人邓某的塑料颗粒加工厂在未取得环保局的环评手续和排污许可证的情况下,将塑料加工时产生的废水直接排放到厂外的渗坑内。严重污染环境。 当天,违法行为人邓某已被行政拘留,案件正在进一步 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |