牌号简介 About |
---|
铝CP-121是为电话和同轴电缆设计的高分子量、低密度聚乙烯化合物。该产品在高速挤压时具有优异的性能,同时电缆表面光滑。该等级包含一个特殊的稳定系统,用于在加工过程中防止热降解和剪切降解,还包含一个金属钝化剂,以确保长期老化性能。典型应用电话电缆的固体绝缘。建议温度分布在150-220°C之间。必须为每条生产线调整最佳的加工条件,建议使用过滤器和隔板来增加气缸中的压力,从而提高电缆质量、均匀性和分散性。彩色电缆Alcudia CP-121上的颜料符合以下规范:ISO 1872 PE KHN 23D003;ASTM D 1248 I,A5,E5级;NF C 32-060 ISM1;VDE 0207 TEIL 2 24I1。 ALCUDIA® CP-121 is high molecular weight, low density polyethylene compound designed for telephone and coaxial cables. This product provides a superior performance at high-speed extrusion together with a smooth surface finish of the cable. This grade contains a special stabilization system for protection against thermal and shear degradation during processing and it also contains a metal deactivator to ensure long-term ageing properties. TYPICAL APPLICATIONS Solid insulation for telephone cables It is recommended a temperature profile between 150 - 220°C. Optimal processing conditions must be tuned for each production line, recommending to use filters and a break plate to increase the pressure in the cylinder and consequently improve the cable quality, homogenization and dispersion of pigments in the case of colored cable ALCUDIA® CP-121 meets the following specifications: ISO 1872 PE KHN 23D003; ASTM D 1248 I, A5, Grade E5; NF C 32-060 ISM1; VDE 0207 Teil 2 24I1. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.921 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.35 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
断裂 fracture |
16.0 | MPa | ISO 527-2 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
600 | % | ISO 527-2 |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
机械性能的保留率 Retention rate of mechanical properties 2 |
|||
100℃ 100℃ 2 |
> 70 | % | ISO 527-2 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature 3 |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
热固性 thermosetting 4 |
|||
200℃ 200℃ 4 |
% | IEC 60811-2-1 | |
氧感应时间 Oxygen sensing time |
|||
200℃ 200℃ |
min | EN 728 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
|||
23℃ 23℃ |
ohms·cm | ASTM D257 | |
介电常数 Dielectric constant |
|||
1 MHz 1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
|||
1 MHz 1 MHz |
ASTM D150 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0 Failures |
3 20 N/cm², 1.9% Peroxide + 0.2% AO |
4 10 days |
【新闻资讯】查看全部
Sabic在欧洲扩展PP风险投资
2017-09-26 9月12日,Sabic在荷兰Geleen地区正式成立了一家新的聚丙烯(PP)试点工厂,并宣布进一步投资建造最先进的PP挤压设备。为支持Sabic公司的2025战略,这两个设备都致力于PP产品的创,通过提供“化学支持”,使其成为化学领域的首选世界领先企业。 根据Sabic对客户驱动创新战略的承诺,位于SABIC全球技术中心的新PP试点工厂将设计下一代PP材料,它已经在使用气相聚合技术。该工厂将进一步促进高创新的材料解决方案的加速开发和商业化,以满足不同行业日益增长的需求,包括 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |