牌号简介 About |
---|
APTIV 1100系列薄膜是由Victrex PEEK聚合物制成的矿物填充半晶体薄膜。该薄膜为超高性能应用的工程师提供了一种材料解决方案。APTIV薄膜是一系列功能广泛、高性能的薄膜,使用它可以降低系统成本、提高性能和增强设计自由度。APTIV 1100具有独特的性能组合,提供高温性能、机械强度、耐久性、优异的辐射、水解和耐化学性、电绝缘、高纯度的优良阻隔性能、不使用阻燃剂的良好易燃性、燃烧产物的低毒性和低薄膜格式的吸湿性。固有的无卤素和易加工性使APTIV薄膜成为我们客户和最终用户的技术推动者。APTIV 1100系列比APTIV 1000系列具有更高的模量和更低的线性热膨胀系数。 APTIV® 1100 series films are the mineral filled semi-crystalline films made from VICTREX® PEEK™ polymer. The film provides a material solution for engineers in ultra-high performance applications. APTIV films are a comprehensive range of versatile, high-performance films, the use of which can facilitate reduced systems costs, improved performance and enhanced design freedom. APTIV 1100 has a unique combination of properties providing high temperature performance, mechanical strength, durability, excellent radiation, hydrolysis and chemical resistance, electrical insulation, excellent barrier properties with high purity, good flammability without the use of flame retardants, low toxicity of combustion products, and low moisture absorption in a film format. Inherently halogen free and ease of processing makes APTIV films a technology enabler for our customers and end users. APTIV 1100 series provides a higher modulus and lower coefficient of linear thermal expansion over the APTIV 1000 series. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density Density |
1.54 | g/cm³ | ISO 1183 |
吸水率 Water Absorption Water Absorption |
|||
平衡 equilibrium,23℃,50% RH,0.05 mm Equilibrium balanced, 23 ℃, 50% RH, 0.05 mm |
0.090 | % | ISO 62 |
成型收缩率 Molding Shrinkage Molding shrinkage |
|||
MD:200℃,50.0 µm MD:200℃,50.0 µm |
% | ||
TD:200℃,50.0 µm TD:200℃,50.0 µm |
% | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness Film thickness |
25 to 125 µm | ||
拉伸模量 Tensile Modulus Tensile Modulus |
ISO 527-3 | ||
MD,23℃,25 µm MD,23℃,25 µm |
5500 | MPa | |
TD,23℃,25 µm TD,23℃,25 µm |
4500 | MPa | |
MD,23℃,50 µm MD,23℃,50 µm |
MPa | ||
TD,23℃,50 µm TD,23℃,50 µm |
MPa | ||
MD,23℃,100 µm MD,23℃,100 µm |
MPa | ||
TD,23℃,100 µm TD,23℃,100 µm |
MPa | ||
拉伸强度 Tensile Strength Tensile Strength |
ISO 527-3 | ||
MD,断裂 brk,23℃,25 µm MD, fracture BRK, 23 ℃, 25 µ m |
MPa | ||
TD,断裂 brk,23℃,25 µm TD, fracture BRK, 23 ℃, 25 µ m |
MPa | ||
MD,断裂 brk,23℃,50 µm MD, fracture BRK, 23 ℃, 50 µ m |
MPa | ||
TD,断裂 brk,23℃,50 µm TD, fracture BRK, 23 ℃, 50 µ m |
MPa | ||
MD,断裂 brk,23℃,100 µm MD, fracture BRK, 23 ℃, 100 µ m |
MPa | ||
TD,断裂 brk,23℃,100 µm TD, fracture BRK, 23 ℃, 100 µ m |
MPa | ||
拉伸应变 Tensile Strain Tensile Strain |
ISO 527-3 | ||
MD,断裂 brk,23℃,25 µm MD, fracture BRK, 23 ℃, 25 µ m |
% | ||
TD,断裂 brk,23℃,25 µm TD, fracture BRK, 23 ℃, 25 µ m |
% | ||
MD,断裂 brk,23℃,50 µm MD, fracture BRK, 23 ℃, 50 µ m |
% | ||
TD,断裂 brk,23℃,50 µm TD, fracture BRK, 23 ℃, 50 µ m |
% | ||
MD,断裂 brk,23℃,100 µm MD, fracture BRK, 23 ℃, 100 µ m |
% | ||
TD,断裂 brk,23℃,100 µm TD, fracture BRK, 23 ℃, 100 µ m |
% | ||
裤型撕裂耐性 Pant shape tear resistance Pant shape tear resistance |
ISO 6383-1 | ||
MD:50 µm MD:50 µm |
N/mm | ||
TD:50 µm TD:50 µm |
N/mm | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
线性热膨胀系数 Coeff.of linear therm expansion Coeff. of linear thermal expansion |
|||
MD:0.05 mm MD:0.05 mm |
1/℃ | ASTM D696 | |
导热系数 Thermal Conductivity Thermal conductivity |
ASTM E1461 | ||
-- -- |
W/m/K | ||
-- -- |
W/m/K | ||
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume Resistivity Volume Resistance |
|||
23 ℃,0.05 mm 23 ℃,0.05 mm |
ohms·cm | ASTM D257 | |
介电强度 Dielectric Strength Dielectric Strength |
|||
23 ℃,0.05 mm 23 ℃,0.05 mm |
kV/mm | ASTM D149 | |
介电常数 Dielectric Constant Dielectric Constant |
|||
23 ℃,0.05 mm,10 MHz 23 ℃,0.05 mm,10 MHz |
ASTM D150 | ||
耗散因数 Dissipation Factor Dissipation Factor |
|||
23℃,0.05 mm,10 MHz 23℃,0.05 mm,10 MHz |
ASTM D150 | ||
补充信息 Supplementary Information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
抗穿刺性 Puncture Resistance Puncture Resistance |
|||
23℃,50.0 µm 23℃,50.0 µm |
kJ/m² | 内部方法 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 24 hrs, 23°C |
3 TM-VX-84 |
4 23°C |
5 below Tg |
6 Through Plane |
7 In-Plane |
8 100 V |
【新闻资讯】查看全部
PTA期价下跌带动现货市场大幅度下跌
2018-11-30 PTA期价下跌带动现货市场大幅度下跌,连续性下跌导致市场心态崩塌,聚酯工厂持续观望操作导致本周现货市场成交清淡,聚酯买盘也以基差后点价交易为主,市场流动性货源难以真正的向下游传导,最终导致现货基差自250元/吨回落至200元/吨附近。 此次下跌主因以成本端塌陷为主,以及对终端经济下行压力担忧加深了市场做空氛围,PTA自身供需格局并未出现明显改观。虽然PTA社会库存仍处于偏低水平,但由于终端需求疲弱导致聚酯工厂持续累库的行情未出现改善,这使得PTA低位社会库存难以左右市场形成 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |