牌号简介 About |
---|
T50-200-178是一种分子量分布窄的高密度聚乙烯共聚物。它适用于要求高抗冲击性和良好抗环境应力开裂性的注塑应用。该材料符合21 CFR 177.1520的食品和药品管理局要求。 T50-200-178 is a high density polyethylene copolymer with narrow molecular weight distribution. It is intended for injection molding applications which require high impact resistance and good environmental stress crack resistance. This material meets the Food and Drug Administration requirements of 21 CFR 177.1520. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.952 | g/cm³ | ASTM D4883 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
2.0 | g/10min | ASTM D1238 |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
100%非离子洗涤剂,F50 100% non-ionic detergent, F50 |
16.5 | hr | ASTM D1693B |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
68 | ASTM D2240 | |
拉伸强度 tensile strength 2 |
|||
断裂 fracture 2 |
35.2 | MPa | ASTM D638 |
屈服 yield 2 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 2 |
|||
断裂 fracture 2 |
% | ASTM D638 | |
屈服 yield 2 |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
正切 tangent |
MPa | ASTM D790-A | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
Area Area |
kJ/m² | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
【新闻资讯】查看全部
中国高分子管道和容器学术委员会贵宾莅临博创交流指点
2016-11-30 2016年11月29日上午,中国高分子管道和容器学术委员会贵宾一行到访博创广州总部交流指导,博创朱康建董事长、营销公司袁中华总经理出席接待,对郑老师等专家一行的到来表示热烈的欢迎。 朱董致词,热烈欢迎郑老 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |