牌号简介 About |
---|
HANWHA LLDPE HS1600是由Unipol工艺生产的高强度LLDPE,设计用于拉伸包装。LLDPE HS1600具有优异的力学性能、拉伸性能、光学性能和退绕性能。 HANWHA LLDPE HS1600 is high strength LLDPE manufactured by Unipol process and designed for stretch wrap. LLDPE HS1600 has excellent mechanical property, stretchability, optical properties and unwinding properties. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.917 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
3.2 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
20 | µm | |
拉伸强度 tensile strength |
ASTM D882 | ||
断裂 fracture |
34.3 | MPa | ASTM D638 |
MD,断裂,20 µm MD, fracture, 20 µ m |
44.1 | MPa | ASTM D882 |
TD,断裂,20 µm TD, fracture, 20 µ m |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
断裂 fracture |
% | ASTM D638 | |
MD,断裂,20 µm MD, fracture, 20 µ m |
% | ASTM D882 | |
TD,断裂,20 µm TD, fracture, 20 µ m |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
20 µm 20 µm |
g | ASTM D1709-B | |
撕裂强度 tear strength |
ASTM D1004 | ||
MD,20 µm MD,20 µm |
kN/m | ASTM D1004 | |
TD,20 µm TD,20 µm |
kN/m | ASTM D1004 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
熔融峰值温度 Melting peak temperature |
℃ | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
雾度 Haze |
|||
20 µm 20 µm |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
【生活中的LG化学】延长柏油路的寿命,沥青改质剂
2020-09-20 搜料网资讯: 行驶在公路上,我们经常能看到裂痕和坑坑洼洼的路面。 尤其在沥青公路上 更 为多见。 沥青铺路具有施工时间短、维护方便等优点,但同时也 具 有受热易变形、低温易 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |