牌号简介 About |
---|
Hysol ES1900是一种透明、中等粘度的环氧树脂配方,推荐用于需要透明性和优良结构、机械和电气性能的小型封装和层压应用。这种由两部分组成的粘合剂具有良好的润湿性,在室温下固化,并与大多数材料(包括光纤、玻璃陶瓷、大多数金属和许多硬质塑料)形成强而低的收缩键。在较宽的温度范围内具有良好的尺寸稳定性。完全固化,是一种持久耐用的电绝缘体,具有良好的物理性能和优异的耐化学性。该产品通常用于-60°C至+125°C的操作范围。 HYSOL® ES1900™ is a transparent, medium-viscosity epoxy resin formulation recommended for small potting and laminating applications where clarity and excellent structural, mechanical and electrical properties are required. This two-part adhesive exhibits good wetting, cures at room temperature and develops strong, low shrinkage bonds to most materials including optical fibers, glass ceramics, most metals and many rigid plastics. It has excellent dimensional stability over a wide temperature range. Fully cured, it is a durable electrical insulator with good physical properties, and excellent chemical resistance. This product is typically used in applications with an operating range of -60°C to +125°C. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
吸水率 Water absorption rate |
|||
24hr 24hr |
0.30 | % | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
玻璃化转变温度 Glass transition temperature |
80.0 | ℃ | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
|||
< 80℃ < 80℃ 2 |
6.8E-5 | cm/cm/℃ | |
> 80℃ > 80℃ 3 |
1.9E-4 | cm/cm/℃ | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity 4 |
3.0E+16 | ohms | |
体积电阻率 Volume resistivity |
|||
25 ℃ 25 ℃ |
ohms·cm | ||
介电强度 Dielectric strength |
kV/mm | ||
介电常数 Dielectric constant |
|||
25 ℃,1 kHz 25 ℃,1 kHz |
|||
耗散因数 Dissipation factor |
|||
25℃,1 kHz 25℃,1 kHz |
|||
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
重量混合比(PBW) Weight Mix Ratio (PBW) |
|||
Part A Part A |
|||
Part B Part B |
|||
体积混合比(PBV) Volume Mixing Ratio (PBV) |
|||
Part A Part A |
|||
Part B Part B |
|||
密度 Density |
|||
25℃ 25℃ 5 |
g/cm³ | ||
-- -- 6 |
g/cm³ | ||
25℃ 25℃ 7 |
g/cm³ | ||
粘度 viscosity |
|||
25℃ 25℃ 5 |
Pa·s | ||
25℃ 25℃ 6 |
Pa·s | ||
25℃ 25℃ 7 |
Pa·s | ||
固化时间 Curing time |
|||
25℃ 25℃ |
hr | ||
胶凝时间 Gelation time 8 |
|||
25℃ 25℃ 8 |
min | ||
储存稳定性 storage stability 8 |
|||
25 ℃ 25 ℃ 8 |
min | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
|||
拉伸强度 tensile strength |
MPa | ||
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ||
弯曲强度 bending strength |
MPa | ||
压缩强度 compressive strength |
MPa |
备注 |
---|
2、Alpha 1 |
3、Alpha 2 |
4、25°C |
5、Part B |
6、Mixed |
7、Part A |
8、100 g mass |
【新闻资讯】查看全部
新疆“煤改电”将从南疆拓展到全疆
2021-03-23 搜料网资讯: 2月5日下午,新疆维吾尔自治区第十三届人民代表大会第四次会议圆满完成各项议程,在新疆人民会堂闭幕。 会议期间,政府工作报告提出,实施煤改电工程。在完成南疆 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |