牌号简介 About |
---|
Ultradur® B 4300 G2是一种易于流动的注射成型PBT,具有10%的玻璃纤维增强,用于刚性、韧性和尺寸稳定的零件。典型应用包括计时器表盘、拨动开关、旋钮、恒温器零件、烤箱门把手、烤面包机外壳和烤架。 Ultradur B 4300 G2 is an easy flowing injection molding PBT with 10% glass fiber reinforcement for rigid, tough, and dimensionally stable parts. Applications Typical applications include timer dials, toggles, knobs, parts for thermostats, oven-door handles, toaster housings and grills. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.37 | g/cm³ | ASTM D792 , ISO 1183 |
熔体体积流动速率 Melt Volume Rate |
|||
250℃,2.16 kg 250℃,2.16 kg |
16.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.80 | % | |
TD TD |
1.4 | % | ISO 294-4 |
MD MD |
1.2 | % | ISO 294-4 |
吸水率 Water absorption rate |
|||
饱和 saturated |
% | ASTM D570 | |
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,50% RH Balance, 50% RH |
% | ASTM D570 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
粘度值 Viscosity value |
|||
降低的粘度 Reduced viscosity |
ml/g | ISO 1628 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
MPa | ASTM D638 , ISO 527-2 | |
断裂,-40℃ Fracture, -40 ℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D638 , ISO 527-2 | |
断裂,-40℃ Fracture, -40 ℃ |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
23℃ 23℃ |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179 | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179 | ||
-30℃ -30℃ |
kJ/m² | ISO 179 | |
23℃ 23℃ |
kJ/m² | ISO 179 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
kJ/m² | ISO 180 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648,ISO 75-2/B | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648,ISO 75-2/A | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 , ISO 3146 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ||
相对温度指数 Relative temperature index |
UL 746 | ||
电气性能 Electrical performance |
UL 746 | ||
0.75 mm 0.75 mm |
℃ | UL 746 | |
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
UL 746 | ||
0.75 mm 0.75 mm |
℃ | UL 746 | |
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
0.75 mm 0.75 mm |
℃ | UL 746 | |
1.50 mm 1.50 mm |
℃ | UL 746 | |
3.00 mm 3.00 mm |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
|||
1.5 mm 1.5 mm |
ohms | ASTM D257 | |
-- -- |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
|||
1.50 mm 1.50 mm |
ohms·cm | ASTM D257 | |
-- -- |
ohms·cm | IEC 60093 | |
介电常数 Dielectric constant |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
杜邦排污致癌赔受害者1250万美元
2017-01-06 北京时间6日凌晨路透社称,美国俄亥俄州一家法院周四作出判决,要求化工巨头杜邦向一名男子支付1050万美元(约合人民币7200万元)的惩罚性损害赔偿金,因为该公司旗下一座化工厂向河水中排放有毒化学物全氟辛酸,致使这名男子患上睾丸癌。 去年12月,一个联邦陪审团已经裁定杜邦向这名男子支付200万美元的补偿性损害赔偿金,周四的判决意味着这名男子总计将获赔1250万美元(约合人民币8600万元)。 自上世纪50年代以来,杜邦位于西弗吉尼亚州的一座工厂就一直向密西西比 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |