牌号简介 About |
---|
高温性能,最容易流动。适用于需要非常薄的墙壁的地方。用于各种SMT应用,尺寸变化最小。30%玻璃填充。化学缩写符合ISO 1043-1:LCP固有阻燃FDA符合UL清单V-0,天然和黑色,厚度为.2 mm,符合UL 94火焰试验。根据UL 746B,相对温度指数(RTI):电气240°C,机械240°C,0.75 mm。保险商实验室(美国) High temperature capability, easiest flow. Suitable where very thin walls are required. Used for broad range of SMT applications, with minimal dimensional change. 30% glass filled. Chemical abbreviation according to ISO 1043-1 : LCP Inherently flame retardant FDA compliant UL- Listing V-0 in natural and black at .2mm thickness per UL 94 flame testing. Relative-Temperature-Index (RTI) according to UL 746B: electrical 240°C, mechanical 240°C at 0.75mm. UL = Underwriters Laboratories (USA) |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.61 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD TD |
0.40 | % | ISO 294-4 |
MD MD |
0.10 | % | ISO 294-4 |
吸水率 Water absorption rate |
|||
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
0.030 | % | ISO 62 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
22 | kJ/m² | ISO 179/1eA |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
kJ/m² | ISO 180/1U | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
8.0 MPa,未退火 8.0 MPa, unannealed |
℃ | ISO 75-2/C | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD TD |
1/℃ | ISO 11359-2 | |
MD MD |
1/℃ | ISO 11359-2 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
|||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
2.05 GHz 2.05 GHz |
Internal Method | ||
耗散因数 Dissipation factor |
|||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
2.05 GHz 2.05 GHz |
Internal Method | ||
耐电弧性 Arc resistance |
sec | 内部方法 | |
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ISO 527-2/1A/1 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ISO 527-2/1A/5 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2/1A/5 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ISO 178 | |
压缩模量 Compression modulus |
MPa | ISO 604 | |
压缩强度 compressive strength |
|||
1% 应变 1% strain |
MPa | ISO 604 | |
断裂弯曲应变 Fracture bending strain |
% | ISO 178 | |
洛氏硬度 Rockwell hardness |
|||
M 级 M-level |
ISO 2039-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 10°C/min |
【新闻资讯】查看全部
细数未来政策对国内聚合MDI的影响
2016-12-01 年底,国内聚合MDI市场人士不仅关注2016年国内的市场回顾及前景,也关注未来政策将对国内聚合MDI市场影响如何,做如下整理: 第一,十三五政策对未来聚合MDI行业发展的影响。 “十三五”期间,聚氨酯泡沫塑料行业发展的重点将围绕“环保、创新、安全、节能、高效、发展”的理念发展,围绕国家的重大产业项目,实现在建筑节能、汽车装备、高速铁路方面的需求增长,实现企业关键技术及装备向规模化、工艺现代化、产品功能化和精细化方向发展,加强公共服务平台建设。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |