牌号简介 About |
---|
TS7006是专为共挤薄膜和层压而开发的低密度聚乙烯(LDPE)。该树脂在机械、光学和刚度性能方面具有很大的结合。除此之外,TS7006凝胶含量低,保证了生产出优良的外观膜。根据ASTM D-4976-04A标准规范,本产品为PE 114。 TS7006 is a low-density polyethylene (LDPE) specially developed for coextruded films and lamination. The resin presents a great combination among mechanical, optical and stiffness properties. Besides TS7006 has low gels content which ensure a production of excellent appearance films. This product is identified as PE 114 according to ASTM D-4976-04a standard specification. Additives: Antiblocking Slip agent Application: High clarity films for coextruded food packaging, such as: cheese, meat, sausages, sliced ham, etc. Process: Blown Film Extrusion |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.925 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.60 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
割线模量 Secant modulus |
|||
2% 正割,TD,40 µm,吹塑薄膜 2% secant, TD, 40 µ m, blow molded film |
170 | MPa | ASTM D882 |
2% 正割,MD,40 µm,吹塑薄膜 2% secant, MD, 40 µ m, blow molded film |
140 | MPa | ASTM D882 |
拉伸强度 tensile strength |
|||
TD,断裂,40 µm,吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
20.0 | MPa | ASTM D882 |
MD,断裂,40 µm,吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
|||
TD,断裂,40 µm,吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
% | ASTM D882 | |
MD,断裂,40 µm,吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
40 µm,吹塑薄膜 40 µ m, blow molded film |
g | ASTM D1709 | |
撕裂强度 tear strength |
|||
TD,40 µm,吹塑薄膜 TD, 40 µ m, blow molded film |
g | ASTM D1922 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
ASTM D2457 | ||
45°,40.0 µm,吹塑薄膜 45 °, 40.0 µ m, blow molded film |
ASTM D2457 | ||
60°,40.0 µm,吹塑薄膜 60 °, 40.0 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
40 µm,吹塑薄膜 40 µ m, blow molded film |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
轻型及高强度处置方案,带来更愉快驾驶体验
2017-03-14 杜邦(DuPont)一直投资于材料研发,并为不同的合作伙伴开发出令人兴奋的应用产品。宝马i8跑车就是这种投资类型的完美一例。宝马i8跑车新的谐振腔采用杜邦™Zytel® PLUS95G35玻璃纤维增强尼龙为原材料。这款谐振腔,由宝马集团、杜邦高性能材料公司和MANN+HUMMEL密切合作共同开发,降低了两个涡轮增压发动机的噪音,带来了更加愉快的驾驶体验。这种材料的轻质和高强度特性还利于减少燃料消耗和CO2 排放。 在不降低性能的同时减少排放的需要,是这种新应用的推动力。汽车 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |