牌号简介 About |
---|
HTA 001HD是一种高分子量的高密度聚乙烯薄膜牌号。 由HTA 001HD制成的薄膜具有卓越的抗冲击性、韧性和高硬度。 HTA 001HD is a high molecular weight HDPE film grade. Films made from HTA 001HD exhibit excellent impact and toughness properties as well as high stiffness. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
190℃,21.6kg 190℃,21.6kg |
9.0 | g/10min | ASTM D1238 |
190℃,5.0kg 190℃,5.0kg |
0.32 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
割线模量 Secant modulus |
ASTM D882 | ||
1% 正割,MD 1% secant, MD |
1200 | MPa | ASTM D882 |
1% 正割,TD 1% secant, TD |
1200 | MPa | ASTM D882 |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服 MD, yield |
41.0 | MPa | ASTM D882 |
TD,屈服 TD, yield |
MPa | ASTM D882 | |
MD,断裂 MD, fracture |
MPa | ASTM D882 | |
TD,断裂 TD, fracture |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂 MD, fracture |
% | ASTM D882 | |
TD,断裂 TD, fracture |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
g | ASTM D1709-A | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD MD |
g | ASTM D1922 | |
TD TD |
g | ASTM D1922 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
中海油计划退出加拿大、英国和美国业务,背后有哪些考量?
2022-04-18 近日有外媒报道称,中国最大的海上石油和天然气生产商中国海洋石油有限公司(下称中海油,0883.HK)正准备退出其在英国、加拿大和美国的业务,寻求出售边际且难以管理的资产。报 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |