牌号简介 About |
---|
法拉第NX07344是一种以PC+ABS共混树脂为基础的复合材料,含有无溴无氯阻燃体系、不锈钢和玻璃纤维。这种材料的附加特性包括:EMI/RFI屏蔽和ESD。 Faradex NX07344 is a compound based on PC+ABS blend resin containing non-brominated and non-chlorinated flame retardant system, Stainless Steel and glass fiber. Added features of this material include: EMI/RFI Shielding and ESD. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.46 | g/cm³ | ASTM D792, ISO 1183 |
收缩率 Shrinkage rate |
内部方法 | ||
MD MD |
0.38 | % | |
TD TD |
0.46 | % | |
吸水率 Water absorption rate |
|||
24hr,50% RH 24hr,50% RH |
0.080 | % | ASTM D570 |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
0.040 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
-- -- 1 |
MPa | ASTM D638 | |
-- -- |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
断裂 fracture 2 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/5 | |
拉伸应变 Tensile strain |
|||
断裂 fracture 3 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/5 | |
弯曲模量 Bending modulus 4 |
|||
50 mm跨距 50 mm span 4 |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
-- -- 5 |
MPa | ISO 178 | |
屈服,50 mm跨度 Yield, 50 mm span 6 |
MPa | ASTM D790 | |
断裂,50 mm跨度 Fracture, 50 mm span 7 |
MPa | ASTM D790 | |
断裂弯曲应变 Fracture bending strain 8 |
% | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 9 |
|||
23℃ 23℃ 9 |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-30℃ -30℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
-30℃ -30℃ 10 |
kJ/m² | ISO 180-1A | |
23℃ 23℃ 11 |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
-30℃ -30℃ |
J/m | ASTM D4812 | |
23℃ 23℃ |
J/m | ASTM D4812 | |
-30℃ -30℃ 12 |
kJ/m² | ISO 180/1U | |
23℃ 23℃ 13 |
kJ/m² | ISO 180/1U | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Total Energy 23℃,Total Energy |
J | ASTM D3763 | |
-- -- |
J | ISO 6603-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,64 mm跨距 1.8 MPa, unannealed, 64 mm span 14 |
℃ | ISO 75-2/Af | |
维卡软化温度 Vicat Softening Temp |
|||
B120 B120 |
℃ | ASTM D1525, ISO 306/B120 12 15 | |
-- -- |
℃ | ASTM D1525 16 | |
A50 A50 |
℃ | ISO 306/A50 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ASTM E831 | |
MD:23~60℃ MD:23~60℃ |
1/℃ | ISO 11359-2 | |
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ASTM E831 | |
TD:23~60℃ TD:23~60℃ |
1/℃ | ISO 11359-2 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
静电衰减 Electrostatic attenuation 17 |
msec | FTMS 101B | |
屏蔽效力 Shielding effectiveness |
内部方法 | ||
1.50 mm 1.50 mm |
dB | ||
3.00 mm 3.00 mm |
dB | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
1.50 mm 1.50 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 类型 1, 0.20 in/min |
4 0.051 in/min |
5 0.079 in/min |
6 Yield |
7 2 mm/min |
8 80*10*4 sp=62mm |
9 80*10*4 |
10 80*10*4 mm |
11 标准 B (120°C/h), 载荷2 (50N) |
12 速率 A (50°C/h), 载荷2 (50N) |
13 5000V to <50V |
【新闻资讯】查看全部
HS一1300型PVC树脂的运用
2018-08-23 HS一1300型PVC树脂为中高分子质量的通用树脂,其孔隙大且均匀、粒度分布窄、增塑剂吸收快,广泛应用于压延或挤出生产软质胶膜、人造革、电缆、管材、软质型材等,也可用于生产注塑制品。 氯化聚乙烯(CPE)是聚乙烯(PE)经氯化反应制得的无规氯化聚合物,具有优良的耐候、耐热老化、耐油、耐化学药品、耐寒、阻燃、抗弯曲开裂等特性,广泛应用于PVC制品的冲击改性,生产屋面防水卷材、矿用阻燃运输带、磁性橡胶、电线电缆、输油输酸胶管等。随着CPE改性PVC制品应用领域的不断开拓,CPE |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |