牌号简介 About |
---|
LL4801N是一种线性低密度聚乙烯,薄膜具有良好的加工性能,平衡了薄膜的机械和光学性能,特别是拉伸薄膜。它含有加工助剂和抗氧化剂添加剂。用途:高性能拉伸薄膜添加剂:加工助剂工艺:LL4801N需要在流延薄膜生产线上加工。挤出温度在220~270°C之间,得到了最佳工艺条件。 LL4801N is a Linear Low Density Polyethylene which the films show good processing performance balanced with excellent mechanical and optical properties, especially for stretch films. It contains processing aid and antioxidant additives. Applications: High performance stretch films Additive: Processing Aid Process: LL4801N need to be processed in cast film lines. The optimum processing conditions are obtained with extrusion temperature between 220 to 270°C. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.917 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
2.1 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
50.0 | MPa | ASTM D882 |
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
40.0 | MPa | ASTM D882 |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
1200 | % | ASTM D882 |
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
% | ASTM D882 | |
弯曲模量 Bending modulus |
ASTM D790 | ||
1% 正割,MD,25 µm,吹塑薄膜 1% secant, MD, 25 µ m, blow molded film |
MPa | ASTM D790 | |
1% 正割,TD,25 µm,吹塑薄膜 1% secant, TD, 25 µ m, blow molded film |
MPa | ASTM D790 | |
落锤冲击 Drop hammer impact |
|||
25 µm,吹塑薄膜 25 µ m, blow molded film |
g | ASTM D1709 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD:25 µm,吹塑薄膜 MD: 25 µ m, blow molded film |
g | ASTM D1922 | |
TD:25 µm,吹塑薄膜 TD: 25 µ m, blow molded film |
g | ASTM D1922 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
60°,25.0 µm,吹塑薄膜 60 °, 25.0 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
25 µm,吹塑薄膜 25 µ m, blow molded film |
% | ASTM D1003 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
2024年全球建筑绝热资料规模估计将达349亿美元
2017-08-01 据了解,全球建筑产业价值在2015年已超过7万亿美元,预计到2024年将超过14万亿美元。而作为建筑产业重要一环的建筑绝热材料,因其高节能、减少碳足迹和产品易供性等特性,推动了自身市场的发展。目前,通过建筑物的墙壁、屋顶和地板损失的热量占总体的70%以上,如以最低可能的能源保持室温,则将增加产品渗透。 随着国际能量节约准则(IECC)的普及率增长,刺激了建筑领域的产品发展。此外,政府的规范中呼应了限制温室气体排放和能源节约,这也有望推动建筑绝热材料市场。易于安装、同时拥有高 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |