牌号简介 About |
---|
KM-569IB是一种高流动冲击聚丙烯树脂,用于注塑成型。它具有较高的延伸率和良好的冲击强度。适用于要求熔体流动性高、几何形状复杂的大型制品的注射成型。特点:生产率高,流动性好,延伸性能好,热稳定性好 KM-569IB is s high flow impact PP resin for injection molding applications. It exhibits high elongation as well as good impact strength. It is applicable to the injection molding of large articles which require high melt flowability and complex geometries. Characteristics: High productivity and flowability Excellent elongation properties with good heat stability |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.910 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
60 | g/10min | ASTM D1238 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
59 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
115 | ℃ | ASTM D648 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
85 | ASTM D785 | |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
中国中化尼龙66新材料项目装置一次开车成功
2022-05-10 5月5日,中国中化旗下中化国际扬农集团瑞泰公司位于中化中卫循环经济产业园的尼龙66新材料项目一次开车成功并产出合格产品。 中国中化发布消息称,尼龙66新材料项目历时三年研发 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |