pH0952是一种熔融指数中等的聚丙烯均聚物,含有助滑剂和防堵剂。PH0952是专为铸造和吹塑薄膜挤出工艺膜段和包装而设计的。它具有良好的透明度和光泽度,并且具有很好的加工性能。 PH 0952 is a medium melt flow rate homopolymer, with slip and antiblocking agents. This product is designed for technical films segment and packaging for cast and blown film extrusion. This product features excellent optical properties and good processability. Applications: Coil for automatic packaging; Food and textile packaging; Films for lamination. Processing: Blown Film Extrusion Cast Film Extrusion |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.905 | g/cm³ | ASTM D792 |
密度 Density |
0.905 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
8.0 | g/10min | ISO 1133 |
230℃,2.16kg 230℃,2.16kg |
8.0 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
割线模量 Secant modulus |
|||
1% 正割,TD,吹塑薄膜 1% secant, TD, blow molded film |
550 620 | MPa | ASTM D882 |
1% 正割,MD,吹塑薄膜 1% secant, MD, blow molded film |
MPa | ASTM D882 | |
拉伸强度 tensile strength |
|||
屈服,注塑成型 Yield, injection molding |
MPa | ISO 527-2 | |
屈服,注塑成型 Yield, injection molding |
MPa | ASTM D638 | |
TD,屈服,吹塑薄膜 TD, yield, blow molded film |
MPa | ASTM D882 | |
MD,屈服,吹塑薄膜 MD, yield, blow molded film |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
|||
屈服,注塑成型 Yield, injection molding |
% | ISO 527-2 | |
屈服,注塑成型 Yield, injection molding |
% | ASTM D638 | |
TD,屈服,吹塑薄膜 TD, yield, blow molded film |
% | ASTM D882 | |
MD,屈服,吹塑薄膜 MD, yield, blow molded film |
% | ASTM D882 | |
密封起始温度(吹塑薄膜) Sealing starting temperature (blow molded film) |
℃ | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃,注塑成型 23 ℃, injection molding |
J/m | ASTM D256 | |
23℃,注塑成型 23 ℃, injection molding |
kJ/m² | ISO 180 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,注塑 1.8 MPa, unannealed, injection molded |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火,注塑成型 0.45 MPa, unannealed, injection molded |
℃ | ASTM D648 | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 3 | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,吹塑薄膜 45 °, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
吹塑薄膜 Blown film |
% | ASTM D1003 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
弯曲模量 Bending modulus |
|||
1% 正割,注塑成型 1% cut, injection molding |
MPa | ISO 178 | |
1% 正割,注塑成型 1% cut, injection molding |
MPa | ASTM D790 | |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level 2 |
ISO 2039-2 | ||
R 级 R-level |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 压 力1 (10N) |