牌号简介 About |
---|
DAI-EL G-902 DAI-EL™ G-902是一种低粘度三元共聚物,适用于各种过氧化物固化系统。可配制G-902以消除后固化过程。G-902设计用于压缩、转移、挤压和注射成型应用,需要良好的耐化学性和蒸汽性。DAI-EL G-902 DAI-EL™ G-902是一种含氟弹性体,由偏二氟乙烯/四氟乙烯/六氟丙烯三元共聚物组成。这种材料可以用过氧化物固化。该材料具有最高氟含量等级,与多元醇固化系列相比具有优异的机械性能、耐酸性、耐蒸汽性和耐化学性和流动性。 DAI-EL® G-902 DAI-EL® G-902 is a terpolymer suitable for various peroxide cure systems. DAI-EL® G-902 can be formulated to eliminate the post cure process. DAI-EL® G-902 is suitable for transfer and compression molding applications requiring excellent chemical and steam resistance. DAI-EL® G-902 DAI-EL G-902 is a fluoroelastomer comprising terpolymer of vinylidenefluoride/tetrafluoroethylene/hexafluoropropylene. This material can be cured by peroxide. This material is of the grade of the highest fluorine content and provides excellent mechanical properties, acid, steam and chemical resistance and good flowability in comparison to polyol cure series. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.87 到 1.91 | g/cm³ | |
门尼粘度 Mooney viscosity |
|||
ML 1+10,121℃ ML 1+10,121℃ |
19 | MU | |
氟含量 Fluorine content |
71 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A,25℃ Shore A, 25 ℃ |
70 | ||
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服,25℃ Yield, 25 ℃ |
22.0 | MPa | |
100% 应变,25℃ 100% strain, 25 ℃ |
MPa | ||
拉伸应变 Tensile strain |
|||
断裂,25℃ Fracture, 25 ℃ |
% | ||
撕裂强度 tear strength |
|||
25℃ 25℃ |
kN/m | ||
压缩形变 Compression deformation |
|||
25℃,70 hr 25℃,70 hr |
% | ||
100℃,70 hr 100℃,70 hr |
% | ||
175℃,70 hr 175℃,70 hr |
% | ||
200℃,70 hr 200℃,70 hr |
% | ||
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 The rate of change in tensile strength in air |
|||
230℃,70 hr 230℃,70 hr |
% | ||
空气中极限伸长率的变化率 The rate of change in ultimate elongation in air |
|||
230℃,70 hr 230℃,70 hr |
% | ||
空气中硬度计硬度的变化率 The rate of change in hardness of a hardness tester in the air |
|||
邵氏 A,230℃,70 hr Shore A, 230 ℃, 70 hr |
|||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
固化温度 curing temperature |
℃ | ||
固化时间 Curing time |
|||
Curelastmeter Curelastmeter |
min | ||
Gehman Torsion Test Gehman Torsion Test |
|||
T10 T10 |
℃ | ||
T2 T2 |
℃ | ||
TR Test TR Test |
|||
TR10 TR10 |
℃ | ||
TR70 TR70 |
℃ |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 23°C |
3 25% compression |
【新闻资讯】查看全部
PTA疯涨遇“告发信”热议连连,惨遭跌停,下游聚酯备受煎熬
2019-07-08 PTA是什么?PTA涨跌与塑料有什么关系呢?为什么我们要讲PTA,接下来一一说明。 解密PTA,多塑料原料的直接上游 PTA学名精对苯二甲酸,源头是原油,直接原料是PX(对二甲苯),原油和 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |