牌号简介 About |
---|
KOPELEN JM-370K是高抗冲嵌段共聚物,具有较高的乙丙橡胶含量。通过对模具的脱模和防静电性能的改进,使该级产品能够在大型注塑设备上进行加工。KOPELEN JM-370K具有较高的熔体流动性,具有良好的强度平衡和抗冲击性能。 Description JM-370K is high impact block copolymer which has high ethylene-propylene rubber content. This grade is designed to be processed in huge Injection molding equipments by improvement in mold release and anti-static. JM-370K show high melt flow and has good balance of strength, impact resistance. Applications Huge home appliances case & cover Base resin for compounding |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.900 | g/cm³ | ASTM D792 , ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
30 | g/10min | ASTM D1238,ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服 yield |
26.0 | MPa | ASTM D638 |
屈服 yield |
25.0 | MPa | ISO 527-2 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
> 50 | % | ASTM D638 |
断裂 fracture |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
-- -- |
MPa | ASTM D790 | |
-- -- |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-10℃ -10℃ |
J/m | ASTM D256 | |
-10℃ -10℃ |
J/m | ISO 180 | |
23℃ 23℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ISO 180 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
新设计:透明可印刷塑料具有高导电性
2023-01-04 扫描上图二维码,可以免费下载 搜料 APP 近日,美国机械工程研究科学家詹姆斯庞德和佐治亚理工学院的研究人员设计出一种透明聚合物薄膜。这种薄膜可以像其他常用材料一样有效地 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |