牌号简介 About |
---|
NANCAR® 1053X26是一种中等耐油性的中低丙烯腈-丁二烯共聚物。它在低温下聚合,并含有足够的抗氧化剂,以满足正常老化条件。具有较低的门尼粘度,加工性能优越。建议的用途包括需要改进低温性能的应用。NANCAR® 1053X26提供卓越的挤压和一般的加工改进。 NANCAR® 1053X26 is a medium low acrylonitrile butadiene copolymer with medium oil resistance. It is polymerized at low temperature and contains sufficient antioxidant for normal aging conditions. It has low Mooney viscosity, and has superior processing characteristics. Suggested usages include applications which require improved low temperature properties. NANCAR® 1053X26 provides excellent extrusions and general processing improvement. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.960 | g/cm³ | |
门尼粘度 Mooney viscosity |
|||
ML 1+4,100℃ ML 1+4,100℃ |
52 | MU | ASTM D1646 |
丙烯腈含量(Bound) Acrylonitrile content (Bound) |
26.0 | % | 内部方法 |
Stabilizer Stabilizer |
Non-staining | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ASTM D2240 | ||
邵氏 A Shaw's A 2 |
66 | ASTM D2240 | |
邵氏 A Shaw's A 3 |
ASTM D2240 | ||
邵氏 A Shaw's A 4 |
ASTM D2240 | ||
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D412 | ||
300% 应变 300% strain 5 |
MPa | ASTM D412 | |
300% 应变 300% strain 6 |
MPa | ASTM D412 | |
300% 应变 300% strain 7 |
MPa | ASTM D412 | |
拉伸强度 tensile strength |
ASTM D412 | ||
屈服 yield 2 |
MPa | ASTM D412 | |
屈服 yield 3 |
MPa | ASTM D412 | |
屈服 yield 4 |
MPa | ASTM D412 | |
拉伸应变 Tensile strain |
ASTM D412 | ||
断裂 fracture 5 |
% | ASTM D412 | |
断裂 fracture 6 |
% | ASTM D412 | |
断裂 fracture 7 |
% | ASTM D412 | |
撕裂强度 tear strength 8 , 3 |
kN/m | ASTM D624 | |
压缩形变 Compression deformation 4 |
|||
100℃,70 hr 100℃,70 hr 4 |
% | ASTM D395 | |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 The rate of change in tensile strength in air 3 |
|||
100℃,70 hr 100℃,70 hr 3 |
% | ASTM D865 | |
空气中极限伸长率的变化率 The rate of change in ultimate elongation in air 3 |
|||
100℃,70 hr 100℃,70 hr 3 |
% | ASTM D865 | |
空气中硬度计硬度的变化率 The rate of change in hardness of a hardness tester in the air 3 |
|||
邵氏 A,100℃,70 hr Shore A, 100 ℃, 70 hr 3 |
ASTM D865 | ||
拉伸强度的变化率 The rate of change in tensile strength 3 |
ASTM D471 | ||
100℃,70 hr,在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ASTM D471 | |
100℃,70 hr,在ASTM #3油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ASTM D471 | |
极限伸长率的变化率 Change rate of ultimate elongation 3 |
ASTM D471 | ||
100℃,70 hr,在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ASTM D471 | |
100℃,70 hr,在ASTM #3油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ASTM D471 | |
邵氏硬度的变化率 The rate of change in Shore hardness 3 |
ASTM D471 | ||
支撐 A,100℃,70 hr,在ASTM #1油中 Support A, 100 ℃, 70 hr, in ASTM # 1 oil |
ASTM D471 | ||
支撐 A,100℃,70 hr,在ASTM #3油中 Support A, 100 ℃, 70 hr, in ASTM # 3 oil |
ASTM D471 | ||
体积变化 Volume change 3 |
ASTM D471 | ||
100℃,70 hr,ASTM 标准油(1号) 100 ℃, 70 hr, ASTM standard oil (No.1) |
% | ASTM D471 | |
100℃,70 hr,ASTM 标准油(3号) 100 ℃, 70 hr, ASTM standard oil (No.3) |
% | ASTM D471 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热损耗 Heat loss |
% | ASTM D5688 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 硫化 20.0 min 在 302°F |
3 硫化 40.0 min 在 302°F |
4 硫化 60.0 min 在 302°F |
5 Cured for 60.0 min at 150°C |
6 Cured for 40.0 min at 150°C |
7 Cured for 20.0 min at 150°C |
8 C 模具 |
【新闻资讯】查看全部
简述PET塑料的改性类型
2017-09-12 化学改性 乙丙胶化学改性在乙丙胶中加入过氧化物或硫化物,用过氧化物为固化剂时,弹性体与塑化相都会受到不同程度的影响,过氧化物攻击弹性体与聚合物,生成活性基团,导致更多的有效交联,产生分子链段的缠结,缠结越大引起收缩越大。但过氧化物用量必须严格控制,过量会使交联困难,整体冲击强度下降。 三元乙丙胶的接枝反应由于三元乙丙胶不含极性基团,因此与极性聚合物的相容性很差,用高沸点 低毒性的马来酸二丁酯进行熔融接枝,在其烃链上接入极性基团,制得功能化的聚合物,改善了它与 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |