牌号简介 About |
---|
RADEL R-7159预着色聚苯砜(PPSU)树脂已开发用于商用飞机内部,具有严格的颜色要求。该产品符合美国联邦航空局(FAA)14CFR第25部分附录F的适用规定,在俄亥俄州立大学(OSU)热释放率法中提供垂直可燃性、极低的发烟量和较低的热释放值。它还产生低燃烧模式的有毒气体排放。该树脂对航空工业中发现的大多数液体(包括清洁剂和杀虫剂)具有良好的抵抗力。本产品可提供与原始设备制造商颜色标准相匹配的着色等级。可用等级包括:白色:Radel R-7159 WH 70913白色:Radel R-7159 WH 7363蓝色:Radel R-7159 BU 7923灰色:Radel R-7159 GY 714 Radel® R-7159 pre-colored polyphenylsulfone (PPSU) resins have been developed for commercial aircraft interior applications with strict color requirements. The product complies with applicable FAA regulation 14CFR Part 25 Appendix F, offering vertical flammability resistance, very low smoke generation and low heat release values in the Ohio State University (OSU) rate of heat release method. It also generates low flaming-mode toxic gas emissions. The resin offers good resistance to most fluids found in the aviation industry including cleaning agents and pesticides. This product is available in pigmented grades to match OEM color standards. Available grades include: White: Radel® R-7159 WH 70913 White: Radel® R-7159 WH 7363 Blue: Radel® R-7159 BU 7923 Gray: Radel® R-7159 GY 714 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.43 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
380℃,2.16kg 380℃,2.16kg |
19 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
> 2410 | MPa | ASTM D638 |
拉伸强度 tensile strength |
|||
屈服 yield |
> 68.9 | MPa | ASTM D638 |
拉伸应变 Tensile strain 2 |
|||
断裂 fracture 2 |
> 10 | % | ASTM D638 |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
OSU峰值放热速率 OSU peak heat release rate 3 |
kW/m² | FAR 25, AppF | |
OSU总放热量(2分钟) OSU total heat release (2 minutes) 3 |
kW·min/m² | FAR 25, AppF | |
垂直燃烧-60秒 Vertical combustion -60 seconds 3 |
|||
滴液燃烧时间 Droplet combustion time |
|||
燃烧时间 Burning time |
sec | ||
长度 length |
cm | ||
毒气排放 Toxic gas emissions 3 |
|||
CO CO |
ppm | ||
HCL HCL |
ppm | ||
HCN HCN |
ppm | ||
HF HF |
ppm | ||
NO+NO2 NO+NO2 |
ppm | ||
SO2 SO2 |
ppm | ||
|
Ds | FAR 25, AppF | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
备注 |
---|
2、51 mm/min |
3、可燃性试验结果的目的不是为了反映这些或任何其他材料在实际火灾条件下的危险性。 |
【新闻资讯】查看全部
巴斯夫与诺镍(Norilsk Nickel)开展独家协作会谈
2017-06-30 德国路德维希港,俄罗斯莫斯科,中国上海 ― 2017年6月28日 ― 巴斯夫与诺镍(PJSC MMC Norilsk Nickel)今日(欧洲时间27日)宣布,双方已签署谅解备忘录,并就未来欧洲锂电行业提供电池材料及其原料开展独家合作谈判。首先,巴斯夫将投资4亿欧元在欧洲建造行业领先的正极材料生产装置。依照预期协议,巴斯夫将从位于芬兰哈尔亚瓦尔塔的诺镍金属冶炼厂获得原材料,诺镍位于俄罗斯的矿源将保障镍、钴原料的稳定供应。除了在原材料市场的领先地位,诺镍也将为本次合作带来极为丰富的金属冶炼与 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |