牌号简介 About |
---|
IROGRAN® A 75 P 4655 N是一种黑色聚醚基热塑性聚氨酯,用于注塑成型。IROGRAN® A 75 P 4655 N是亨斯迈注塑产品系列的一部分。它可以在低温下进行加工,并提供一种特别设计的、灵活的材料,适用于成型。性能特点:良好的环境和低温灵活性,短周期时间无邻苯二甲酸盐,良好的熔体流动性,易于脱模,良好的水解和微生物抗性。 IROGRAN A 75 P 4655 N is a black colored polyether based thermoplastic polyurethane intended for injection moulding applications. IROGRAN A 75 P 4655 N is a part of the HUNTSMAN injection moulding product range. It is processable at low temperatures and offers a specially designed, flexible material suitable for mouldings. PERFORMANCE FEATURES Excellent ambient & low temperature flexibility Short cycle times Phthalate free Good melt flow Easy demoulding Excellent hydrolysis & microbial resistance |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density 2 |
1.12 | g/cm³ | ASTM D792 |
熔体体积流动速率 Melt Volume Rate |
|||
190℃,10 kg 190℃,10 kg |
50.0 | cm³/10min | |
收缩率 Shrinkage rate |
|||
MD:注塑成型 MD: Injection molding |
0.80 | % | 内部方法 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
DIN 53505 | ||
邵氏 A,注塑成型 Shaw A, injection molding |
73 | DIN 53505 | |
邵氏 D,注塑成型 Shaw's D, injection molding |
23 | DIN 53505 | |
邵氏硬度 Shore hardness |
ASTM D2240 | ||
邵氏 A,注塑成型 Shaw A, injection molding |
ASTM D2240 | ||
邵氏 D,注塑成型 Shaw's D, injection molding |
ASTM D2240 | ||
Abrasion Abrasion 2 |
mm³ | DIN 53516 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 3 |
|||
断裂,0.635 mm Fracture, 0.635 mm 3 |
MPa | DIN 53504 | |
300% 应变,0.635 mm 300% strain, 0.635 mm 3 |
MPa | DIN 53504 | |
100% 应变,0.635 mm 100% strain, 0.635 mm 3 |
MPa | DIN 53504 | |
拉伸应变 Tensile strain 3 |
|||
断裂,0.635 mm Fracture, 0.635 mm 3 |
% | DIN 53504 | |
撕裂强度 tear strength 3 |
|||
0.635 mm 0.635 mm 3 |
kN/m | DIN 53515 | |
压缩形变 Compression deformation 2 |
ASTM D395 | ||
23℃,24 hr 23℃,24 hr |
% | ASTM D395 | |
70℃,24 hr 70℃,24 hr |
% | ASTM D395 | |
压缩形变 Compression deformation 2 |
DIN 53517 | ||
23℃,24 hr 23℃,24 hr |
% | DIN 53517 | |
70℃,24 hr 70℃,24 hr |
% | DIN 53517 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
TMA TMA 3 |
Internal Method | ||
High:635.0 µm High:635.0 µm |
℃ | Internal Method | |
Low:635.0 µm Low:635.0 µm |
℃ | Internal Method |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Injection Molded |
3 Extruded Film |
【新闻资讯】查看全部
3D打印塑料模具会取代传统机加工模具吗?
2016-10-19 许多3D打印支持者声称,3D打印对需要开模具的注塑成型是个很好的代替。真的是这样吗?下面我们一起去看看大家的意见是怎么样的? 增材制造(大家所熟知的3D打印)已经给制造业带来了巨大影响。那些曾经需要几百美元、耗时几周的手板件,现在可以早上设计、晚上打印,第二天早上就可以送达客户手里。 有些公司已经在使用3D打印工艺制造注塑模具。不再需要花费几个月时间来等待可以用于生产的模具的制造,或者因为下游设计变化导致修改模具的大量金钱投入,或者生产层上的不确定因素。不管 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |