牌号简介 About |
---|
沙特基础工业公司(SABIC)的高密度聚乙烯(HDPE)级产品在受控条件下生产,产品质量高、一致性好、纯度高。SABIC® HDPE PCG863通常用于医疗包装、盖和封口以及医疗包装的其他零件的注塑成型。这是一个容易加工,硬度等级。遵守法规。SABIC® HDPE PCG863符合欧洲药典(EP)和美国药典(USPVI)的相关专著。 SABIC® HDPE grades for healthcare applications are produced under controlled conditions resulting in high product quality, consistency and a high level of purity. SABIC® HDPE PCG863 is typically used for the injection moulding of healthcare packaging, caps and closures and other parts for medical packaging. It is an easy-to-process, stiff grade. Compliance to regulations. SABIC® HDPE PCG863 complies with the relevant monographs of the European Pharmacopoeia (EP) and the United States Pharmacopoeia (USPVI). |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.963 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
ISO 1133 | ||
190℃,2.16kg 190℃,2.16kg |
8.0 | g/10min | ISO 1133 |
190℃,5.0kg 190℃,5.0kg |
23 | g/10min | ISO 1133 |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
40 ℃,1.00 mm,10%润湿剂,模压成型 40 ℃, 1.00 mm, 10% wetting agent, molded |
8.00 | hr | 内部方法 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃,模压成型 23 ℃, molded |
4.0 | kJ/m² | ISO 180-A |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | ISO 11357-3 | |
Enthalpy Change Enthalpy Change |
J/g | ISO 11357-3 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,模压成型 Shaw's D, molded |
ISO 868 | ||
拉伸模量 Tensile modulus |
|||
2 mm,模压成型 2 mm, molded into shape |
MPa | ISO 527-2/1BA/50 | |
拉伸强度 tensile strength |
ISO 527-2/1BA/50 | ||
屈服,2 mm,模压成型 Yield, 2 mm, molded |
MPa | ISO 527-2/1BA/50 | |
断裂,2 mm,模压成型 Fracture, 2 mm, molded |
MPa | ISO 527-2/1BA/50 | |
拉伸应变 Tensile strain |
|||
断裂,2 mm,模压成型 Fracture, 2 mm, molded |
% | ISO 527-2/1BA/50 | |
弯曲模量 Bending modulus |
|||
2 mm,模压成型 2 mm, molded into shape |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
2 mm,模压成型 2 mm, molded into shape |
MPa | ISO 178 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2 MPa |
【新闻资讯】查看全部
年产7万吨!万华化学一期界面光气法聚碳酸酯装置投产
2018-01-24 近日,万华化学烟台工业园一期7万吨/年界面光气法聚碳酸酯(PC)装置成功实现连续化生产。该界面光气法装置是万华化学历经十余载艰苦卓绝的自主研发而成,具有完全自主知识产权。 历经十余载艰苦卓绝的自主研发,万华化学烟台工业园一期7万吨/年界面光气法聚碳酸酯(PC)装置于近日成功实现连续化生产,并产出高品质合格产品。 该系列产品已在市场上获得广泛认可,多家国内外知名品牌客户已与万华化学达成了2018年战略合作协议。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |