牌号简介 About |
---|
TIPELIN® FS 383-03是中等密度聚乙烯共聚物(以己烯-1为共聚单体)的薄膜级。该产品具有很好的Elmendorf撕裂强度和抗飞镖跌落性能。该等级包含抗氧化剂和酸清除剂。推荐应用TIPELIN® FS 383-03用于塑料袋、购物袋、多层薄膜和低密度聚乙烯混合组分。TIPELIN® FS 383-03适用于食品接触和制药包装产品的制造。产品符合食品接触法规。 TIPELIN FS 383-03 is a film grade of medium density polyethylene copolymer (with hexene-1 as comonomer) grade. The product has very good Elmendorf tear strength and Dart drop resistance. The grade contains antioxidants and acid scavenger. Applications TIPELIN FS 383-03 is recommended for bags, shopping bags, multi-layer films and blend component for LDPE. TIPELIN FS 383-03 is suitable for food contact and for manufacturing of pharmaceutical packing products. The product complies with Food Contact Regulations. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.938 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
ISO 1133 | ||
190℃,2.16kg 190℃,2.16kg |
0.18 | g/10min | ISO 1133 |
190℃,21.6kg 190℃,21.6kg |
15 | g/10min | ISO 1133 |
190℃,5.0kg 190℃,5.0kg |
0.87 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,模压成型 Shaw's D, molded |
60 | ISO 868 | |
弯曲模量 Bending modulus |
|||
模压成型 Compression Molding |
MPa | ISO 178 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
µm | ||
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,屈服,70 µm,吹塑薄膜 MD, yield, 70 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,屈服,70 µm,吹塑薄膜 TD, yield, 70 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,断裂,70 µm,吹塑薄膜 MD, fracture, 70 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,断裂,70 µm,吹塑薄膜 TD, fracture, 70 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸应变 Tensile strain |
ISO 527-3 | ||
MD,断裂,70 µm,吹塑薄膜 MD, fracture, 70 µ m, blow molded film |
% | ISO 527-3 | |
TD,断裂,70 µm,吹塑薄膜 TD, fracture, 70 µ m, blow molded film |
% | ISO 527-3 | |
落锤冲击 Drop hammer impact |
|||
70 µm,吹塑薄膜 70 µ m, blow molded film |
g | ISO 7765-1/A | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ISO 6383-2 | ||
MD:70 µm,吹塑薄膜 MD: 70 µ m, blow molded film |
N | ISO 6383-2 | |
TD:70 µm,吹塑薄膜 TD: 70 µ m, blow molded film |
N | ISO 6383-2 | |
Spencer Impact Spencer Impact |
|||
吹塑薄膜,70.0 µm Blow molded film, 70.0 µ m |
MPa | ASTM D3420 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A120 | |
氧化诱导时间 Oxidation induction time |
|||
模压成型,200℃ Compression molding, 200 ℃ |
min | EN 728 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
疫情背后的口罩江湖——极速暴富与债台高筑者的众生相
2021-02-08 搜料网资讯: 湖北仙桃,全国最大的口罩产区,并承担了最多的出口份额 在过去的一年,口罩是全球70亿人每天配戴的必备之物。 作为世界工厂的中国,占据了全球一半左右的口罩产量 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |