牌号简介 About |
---|
高刚度PC/ABS混合物,具有实用的冲击力、低CTE、高耐热性,具有良好的美观性,适用于注塑成型。 High stiffness PC/ABS blend offering practical impact, low CTE, high heat resistance, with good aesthetics suitable for injection molding |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.27 | g/cm³ | ASTM D792 |
熔体体积流动速率 Melt Volume Rate |
|||
260℃,5 kg 260℃,5 kg |
10.0 | cm³/10min | |
265℃,5 kg 265℃,5 kg |
12.0 | cm³/10min | |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.50 到 0.70 | % | |
TD:3.2 mm TD:3.2 mm |
0.50 到 0.70 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
-- -- 2 |
MPa | ASTM D638 | |
-- -- |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
屈服 yield 3 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/5 | |
断裂 fracture 3 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/5 | |
拉伸应变 Tensile strain |
|||
屈服 yield 3 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/5 | |
断裂 fracture |
% | ISO 527-2/5 | |
弯曲模量 Bending modulus 4 |
MPa | ISO 178 | |
弯曲强度 bending strength 4 , 5 |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 6 |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 7 |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Total Energy 23℃,Total Energy |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,4.0 mm,64 mm跨距 1.8 MPa, unannealed, 4.0 mm, 64 mm span 8 |
℃ | ISO 75-2/Af | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ASTM E831 | |
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ASTM E831 | |
TD:-40℃ TD:-40℃ |
1/℃ | ISO 11359-2 |
备注 |
---|
2. 5.0 mm/min |
3. 类型 1, 5.0 mm/min |
4. 2.0 mm/min |
5. at Yield |
6. 80*10*3 sp=62mm |
7. 80*10*3 mm |
8. 80*10*4 mm |
【新闻资讯】查看全部
东华机械高层谈企业提高与行业开展
2016-11-21 东华机械日前举行年末大型记者见面会,十余家中央、省、市重点媒体参加,东华机械母公司──大同机械企业有限公司执行董事兼行政总裁邓愚先生也参加会见。 据了解,2016年东华机械注塑机中国销售增长15%,营业额上升了一个台阶,产品性价比整体提升,客户认可度增强,东华机械与市场互动进入良性循环。 邓总表示,2017年东华机械将持续“四精战略”,深化产品结构优化,集中优势资源,在产品智能化,产品专业化等方面进行全面提升,形成可持续发展的企业竞争优势。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |