牌号简介 About |
---|
GP100ORXP是一种高密度聚乙烯化合物,专门开发用于制造气体分配用挤压管。采用双峰技术生产,摩尔质量高。它具有优良的机械性能和抗静水压力和应力开裂性能。根据ISO 9080,该树脂的MRS(最低要求强度)为10兆帕,根据ISO 12162,该树脂被归类为PE 100。GP100ORXP采用橙色制造,并含有添加剂以防止紫外线辐射和光降解。符合NBR 14462:00和ISO 4437:07的要求。用途:橙色PE 100压力管道配气;水下电缆护套工艺:管道挤出。 GP100ORXP is a High Density Polyethylene compound specially developed for the manufacturing of extruded pipes for gas distribution. It is produced with bimodal technology and has high molar mass. It shows excellent mechanical properties and resistance to hydrostatic pressure and stress cracking. This resin has MRS (Minimum Required Strength) of 10 MPa, according to ISO 9080, and is classified as PE 100, according to ISO 12162. GP100ORXP is manufactured in orange color and contains additives to protect it against ultraviolet radiation action and photodegradation. Meets the requirements of NBR 14462:00 and ISO 4437:07. Application: Orange PE 100 pressure pipes for gas distribution; jacketing of underwater cables Process: Pipe Extrusion. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.948 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,5.0kg 190℃,5.0kg |
0.25 | g/10min | ASTM D1238 |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
ASTM D1693 | ||
50 ℃,2.00 mm,10%非离子表面活性剂,模压成型,F50 50 ℃, 2.00 mm, 10% non-ionic surfactant, molded, F50 |
> 1000 | hr | ASTM D1693 |
50 ℃,2.00 mm,100%非离子表面活性剂,模压成型,F50 50 ℃, 2.00 mm, 100% non-ionic surfactant, molded, F50 |
> 1000 | hr | ASTM D1693 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
模压成型 Compression Molding |
无断裂 | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火,模压成型 0.45 MPa, unannealed, molded |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 2 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,模压成型 Shaw's D, molded |
ASTM D2240 | ||
拉伸强度 tensile strength |
ASTM D638 | ||
屈服,模压成型 Yield, molding |
MPa | ASTM D638 | |
断裂,模压成型 Fracture, molded |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
ASTM D638 | ||
屈服,模压成型 Yield, molding |
% | ASTM D638 | |
断裂,模压成型 Fracture, molded |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
1% 正割,模压成型 1% cut, molded |
MPa | ASTM D790 |
备注 |
---|
2 压 力1 (10N) |
【新闻资讯】查看全部
一文帮你理清4种发泡技术!
2020-09-16 搜料网资讯: 聚合物发泡材料是指以聚合物(塑料、橡胶、弹性体或天然高冷子材料)为基础而其内部具有无数气泡的微孔材料,也可以视为以气体为填料的复合材料。聚合物发泡材料品 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |