Hostalen CRP 100 RT black是一种高密度聚乙烯(HDPE),黑色类似RAL 9004,具有较高的挤出、注射和压塑熔融粘度。该产品被客户用于管道和板材应用中,并提供了优异的抗应力开裂性能(ESCR),即使在高温(RT)下也具有很好的长期静水强度。它具有优良的热老化和极高的萃取稳定性。它不适用于医疗和制药应用。 Hostalen CRP 100 RT black is a high density polyethylene (HDPE), black colored similar RAL 9004, with high melt viscosity for extrusion, injection and compression molding. The product is used by customers in pipe and sheet applications and provides good stress crack resistance properties (ESCR) combined with very good long term hydrostatic strength even at raised temperature (RT). It has an excellent heat ageing and extremely high extraction stability. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.957 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
ISO 1133 | ||
190℃,21.6kg 190℃,21.6kg |
9.5 | g/10min | ISO 1133 |
190℃,5.0kg 190℃,5.0kg |
0.45 | g/10min | ISO 1133 |
炭黑含量 Carbon black content |
2.3 | % | ISO 6964 |
全切口蠕变试验 Full incision creep test 2 |
|||
80℃ 80℃ 2 |
14.6 | day | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Maximum Elongation(TD) Maximum Elongation(TD) |
% | EN 638 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179 | ||
-30℃ -30℃ |
kJ/m² | ISO 179 | |
23℃ 23℃ |
kJ/m² | ISO 179 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
氧感应时间 Oxygen sensing time |
|||
210℃ 210℃ |
min | ISO 11357-6 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Odor Threshold Odor Threshold |
EN 1622/EN 1420 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,3 秒 Shore D, 3 seconds |
ISO 868 | ||
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-2/50 | |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
ISO 527-2/50 | ||
屈服,23℃ Yield, 23 ℃ |
% | ISO 527-2/50 | |
断裂,23℃,4 mm Fracture, 23 ℃, 4 mm |
% | ISO 527-2/50 | |
拉伸蠕变模量 Tensile creep modulus 3 |
ISO 899-1 | ||
1 hr 1 hr |
MPa | ISO 899-1 | |
1000 hr 1000 hr |
MPa | ISO 899-1 | |
弯曲强度 bending strength |
|||
3.50% 应变 3.50% strain |
MPa | ISO 178 | |
弯曲蠕变模量 Bending creep modulus 4 |
DIN 19537-2 | ||
1 min 1 min |
GPa | DIN 19537-2 | |
2000 hr 2000 hr |
GPa | DIN 19537-2 | |
24 hr 24 hr |
GPa | DIN 19537-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 4.0 MPa, 2% Arkopal N 100 |
3 2.0 MPa load |
4 4 point loading method |
【新闻资讯】查看全部
中海油A股IPO首发过会 拟300亿元加码油气布局
2022-02-28 近日,中国证监会披露信息显示,中国海洋石油有限公司A股首发申请获通过。据披露,公司拟公开发行人民币股份数量不超过26亿股并在上交所主板上市。此次募集资金将用于发展公司 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |