牌号简介 About |
---|
Hostacom M4 U02 200007是一种40%滑石填充聚丙烯均聚物,具有高流动性、优异的刚度和高尺寸稳定性。该产品可定制颜色匹配,颗粒形式。此等级为200007彩色版本。该等级不适用于医疗、制药、食品和饮用水应用。 Hostacom M4 U02 200007 is a 40% talc filled PP homopolymer, with high flowability, outstanding stiffness and high dimensional stability. Product is available as a customized color matched, pellet form. This grade is delivered in 200007 color version. This grade is not intended for medical, pharmaceutical, food and drinking water applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.21 | g/cm³ | ISO 1183/A |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
15 | g/10min | ISO 1133 |
熔体体积流动速率 Melt Volume Rate |
|||
230℃,2.16 kg 230℃,2.16 kg |
15.0 | cm³/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
4000 | MPa | ISO 527-2 |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
31.0 | MPa | ISO 527-2 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
0℃ 0℃ |
kJ/m² | ISO 179/1eU | |
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
高光无痕注塑模具设计十大要素
2016-10-28 目前,绝大部分的家用电器外观零部件都是注塑成型得到的。在注塑过程中,易出现熔接痕、气痕、变形等缺陷;高光无痕模具能够解决上述缺陷。下面我们就一起来看看高光无痕注塑模具设计十大要素。 一、高光无痕注塑的原理 1.温度较高 模具成型对温度要求较高(一般为80℃-130℃左右),在注塑转入保压后改用冷却水,使 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |