牌号简介 About |
---|
HANWHA LLDPE HS1700是由Unipol工艺生产的高强度LLDPE,设计用于拉伸包装和尿布薄膜应用。LLDPE HS1600具有优异的力学性能、拉伸性能、光学性能和水蒸气透过率。 HANWHA LLDPE HS1700 is high strength LLDPE manufactured by Unipol process and designed for stretch wrap and diaper film application. LLDPE HS1600 has excellent mechanical property, stretchability, optical properties and water vapor transmittance rate. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.923 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
3.2 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
20 | µm | |
拉伸强度 tensile strength |
ASTM D882 | ||
断裂 fracture |
34.3 | MPa | ASTM D638 |
MD,断裂,20 µm MD, fracture, 20 µ m |
44.1 | MPa | ASTM D882 |
TD,断裂,20 µm TD, fracture, 20 µ m |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
断裂 fracture |
% | ASTM D638 | |
MD,断裂,20 µm MD, fracture, 20 µ m |
% | ASTM D882 | |
TD,断裂,20 µm TD, fracture, 20 µ m |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
20 µm 20 µm |
g | ASTM D1709-B | |
撕裂强度 tear strength |
ASTM D1004 | ||
MD,20 µm MD,20 µm |
kN/m | ASTM D1004 | |
TD,20 µm TD,20 µm |
kN/m | ASTM D1004 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
熔融峰值温度 Melting peak temperature |
℃ | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
雾度 Haze |
|||
20 µm 20 µm |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
面对工业4.0转型热潮 半数中国制造企业尚未做好预备?
2017-05-08 2015年国务院印发《中国制造2025》行动纲领并提出一系列目标后,中国制造业转型正受到全世界的关注。据统计,已有超过1000家国内私募基金与风投涉足工业4.0领域。中国制造业巨头在努力为地方技术供应商或价值链参与者提供赞助和投资,以获得更多的整合机会。中央及地方政府也都在大力投资工业4.0项目。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |