牌号简介 About |
---|
GI-1032是一种高撕裂强度、锡催化的RTV-2硅橡胶,是为中国和陶瓷工业制造外壳模具而设计的。GI-1032在需要更高硬度的情况下也可用于浇注聚氨酯泡沫部件。GI-1032对抑制不敏感,这意味着它几乎可以在任何表面上在室温下固化。它很容易混合和脱气,并将固化只有轻微的收缩。用特殊的活化剂可以加速橡胶硬化的速度。冷凝固化双组分硅橡胶非常适合大多数一般的模具制造和原型应用。它们非常适合铸造蜡、石膏、环氧树脂和其他塑料。对于需要中等硬度的应用,GI-650非常有用。 GI-1032 is a high tear strength, tin-catalyzed RTV-2 silicone rubber, which was designed for making case molds for the china and ceramics industries. GI-1032 is also excellent for casting polyurethane foam parts when a slightly higher hardness is desired. GI-1032 is not sensitive to inhibition, meaning it will cure at room temperature over virtually any surface. It is easy to mix and de-air, and will cure with only a slight degree of shrinkage. The speed at which the rubber hardens can be accelerated with special activators. Condensation cure two-component silicone rubbers are excellent for most general mold making and prototype applications. They are excellent for casting waxes, gypsum, epoxies and other plastics. GI-650 is extremely useful for those applications where a medium durometer is required. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.13 | g/cm³ | |
收缩率 Shrinkage rate |
|||
Cured Cured |
0.10 | % | |
热固性混合粘度 Thermosetting mixed viscosity |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
颜色 colour |
|||
-- -- 2 |
Blue-Green | ||
-- -- 3 |
White | ||
粘度 viscosity |
|||
-- -- 2 |
0.30 到 0.40 | Pa·s | |
-- -- 3 |
Pa·s | ||
固化时间 Curing time |
hr | ||
储存稳定性 storage stability |
min | ||
Cured Properties Cured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A 4 |
|||
邵氏 A Shaw's A 5 |
|||
拉伸强度 tensile strength |
MPa | ASTM D412 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D412 | |
撕裂强度 tear strength |
kN/m | ASTM D624 | |
Coverage(Cured) Coverage(Cured) |
cm³/g | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
使用温度 Operating temperature |
|||
Cured Cured |
℃ | ||
热固组件 Thermosetting components |
|||
树脂 resin |
|||
硬化法 Hardening method |
|||
贮藏期限 Storage period |
wk |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Activator |
3 Base |
4 1 Day |
5 7 Days |
【新闻资讯】查看全部
搜料资讯:美国再延华为的“暂时通用答应证”、华为回应
2019-08-20 1、日本东丽与帝人发力飞机制造轻量碳纤维 近日,日本东丽和帝人两家公司表示,将相继向市场投放用于飞机制造的轻量碳纤维。力争2021年前后开始增加对现有机型的供应,未来飞机 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |