牌号简介 About |
---|
聚苯乙烯525L:是一种低残留的结晶聚苯乙烯,非常适合与透明弹性体混合,用于挤出热成型应用,要求低气味和味道。TOTAL石化产品525L也可以用作共挤应用的盖层,需要有光泽的表面处理,或在注塑成型。注射成型应用,如医疗和实验室零件、制栓和珠宝盒,证明了聚合物在最小应力和快速循环下的成型能力。应用:与透明苯乙烯弹性体混合刀具共挤覆盖医疗应用一般信息:该材料符合21 CFR§177.1640中所述的FDA要求。本材料持有保险商实验室认可94HB;见www.ul.com上的UL文件E55470。USP六级材料安全数据表可帮助客户满足其安全需求。 Polystyrene 525L: Is a crystal polystyrene with low residuals that is ideally suited for blending with clear elastomers for extrusion-thermoforming applications that require low odor and taste. Total Petrochemicals 525L can also be used as a cap layer for coextrusion applications that require a glossy finish, or in injection molding. Injection molding applications such as medical and laboratory parts, tumblers and jewel boxes demonstrate the polymer's ability to be molded with minimal stresses and fast cycles. Application: Blending with clear styrenic elastomers Cutlery Coextrusion capping Medical applications General Information: This material complies with FDA requirements as described in 21 CFR §177.1640. This material holds Underwriters Laboratory recognition 94HB; see UL File E55470 at www.UL.com. USP Class VI Material Safety Data Sheets are available to help customers satisfy their safety needs. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.04 | g/cm³ | |
熔体质量流动速率 Melt Flow Rate |
|||
200℃,5.0kg 200℃,5.0kg |
9.0 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD MD |
0.40 到 0.70 | % | ASTM D955 |
湿度 humidity |
< 0.10 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
3030 | MPa | ASTM D638 |
拉伸强度 tensile strength |
MPa | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
热变形温度 Hot deformation temperature |
|||
退火 annealing |
℃ | ASTM D648 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
国家发改委:油气价格攀升对中国影响可控
2022-03-16 近期,国际原油、天然气价格攀升。对此,国家发改委副主任连维良在上周举行的国新办新闻发布会上表示,由于中国原油、天然气外采比例较高,因此肯定会受到影响,进口成本客观 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |