牌号简介 About |
---|
环氧树脂白色层压系统是一种易于使用的液态环氧树脂系统,适用于各种制造应用。环氧树脂白复合系统未填充,粘度低,无臭,室温固化。固化的环氧树脂具有优异的物理性能。它可以用砂纸打磨、成形、机加工、钻孔、攻丝和喷漆。Epoxamite白色层压系统可与增强材料一起使用,如S-玻璃、E-玻璃、Kevlar和碳纤维,用于叠层应用或复合零件。环氧树脂白色树脂也可以与填充物混合,例如气凝胶二氧化硅应用于胶衣。urefil 3、urefil 7和其他填料可用于整流罩、圆角或粘合应用。 EpoxAmite® White Epoxy Laminating System is an easy-to-use liquid epoxy system formulated for a wide variety of fabrication applications. EpoxAmite® White Laminating System is unfilled, low in viscosity, odorless and cures at room temperature. Cured epoxy displays exceptional physical and performance properties. It can be sanded, shaped, machined, drilled, tapped and painted. EpoxAmite® White Laminating System can be used with reinforcements such as S-Glass, E-Glass, Kevlar and Carbon fibers for lay-up applications or composite parts. EpoxAmite® White Resin can also be mixed with fillers such as fumed silica for gel coat applications. Urefil® 3, Urefil® 7 and other fillers can be added for fairing, filleting or bonding applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.23 | g/cm³ | ASTM D1475 |
特定体积 Specific volume |
0.813 | cm³/g | ASTM D792 |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
固化时间 Curing time 4 |
20.0 到 24.0 | hr | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
85 | ASTM D2240 | |
拉伸模量 Tensile modulus |
3840 | MPa | ASTM D638 |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ||
断裂 fracture 2 |
MPa | ||
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
-- -- 2 |
MPa | ||
-- -- |
MPa | ||
压缩模量 Compression modulus |
MPa | ASTM D695 | |
压缩强度 compressive strength |
MPa | ASTM D695 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
℃ | ASTM D648 | |
热固组件 Thermosetting components |
|||
部件 A Component A |
|||
部件 B Component B |
|||
储存稳定性 storage stability 3 |
min | ASTM D2471 | |
热固性混合粘度 Thermosetting mixed viscosity 3 |
cP | ASTM D2393 | |
工作时间 working hours |
|||
Thin Film Thin Film |
hr |
备注 |
---|
2、6 ply / 10 oz. laminate after 7 days at 73°F / 23°C |
3、100 g |
4、Thin Film |
【新闻资讯】查看全部
天大的曲解!生物可降解塑料�K不更环保
2015-12-25 “生物可降解塑料”因字面意思而被误认为这些塑料最终可在环境中降解、绿色无害,故人们丢弃这种塑料时心理负担不大。 生物可降解塑料�K不更环保 然而,事实与人们的 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |