牌号简介 About |
---|
DuPont™ Teflon ® PTFE DISP 33是一种乳白色的水性聚四氟乙烯分散液,用非离子表面活性剂稳定。Disp 33通常用于玻璃织物的涂层,特别用于提供表面光滑度、粘合性、光泽和可焊性增强的无空隙涂层。经适当处理后,Disp 33中的聚四氟乙烯树脂表现出氟聚合物树脂典型的优越性能:在260°C(500°F)下使用后保持性能,在-240°C(-400°F)下保持有用性能。Disp 33水性分散剂提供:增强表面光滑度、粘合性、光泽和可焊性,几乎对所有工业化学品和溶剂都无惰性,高温下稳定性优异的介电性能任何固体材料的最低摩擦系数优异的耐候性、不粘特性典型应用涂层d建筑、高性能工业、食品加工和电子应用中使用的机织玻璃纤维织物,由编织纤维制成的浸渍填料,用于严重的化学和热应用,用于电容器电介质或化学屏障,金属或其他高温基底的表面涂层,特氟隆聚四氟乙烯P 33符合ASTM D 4441-04,II型,6级,A级的要求。 DuPont™ Teflon ® PTFE DISP 33 is a milky white aqueous PTFE dispersion stabilized with a non-ionic surfactant. DISP 33 is typically used to coat woven glass cloth and has been especially formulated to provide void-free coatings with enhanced surface smoothness, adhesion, gloss and weldability. When properly processed, the PTFE resin in DISP 33 exhibits the superior properties typical of the fluoropolymer resin: retention of properties after service at 260 °C (500 °F), and useful properties at -240 °C (-400 °F). DISP 33 aqueous dispersion provides: enhanced surface smoothness, adhesion, gloss and weldability inertness to nearly all industrial chemicals and solvents stability at high temperatures excellent dielectric properties lowest coefficient of friction of any solid material excellent weatherability non-stick characteristics Typical Applications Coated woven fiber-glass fabric used in architectural, high-performance industrial, food processing and electronics applications Impregnated packing made from braided fibers for severe chemical and thermal service Cast film for capacitor dielectrics or chemical barriers Surface coatings for metallic or other high-temperature substrates Teflon ® PTFE DISP 33 meets the requirements of ASTM D 4441-04, type II, grade 6, class A. |
技术参数 Technical Data | |||
---|---|---|---|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面活性剂含量 - based on PTFE solids Surfactant content - based on PTFE solids |
|||
-- -- |
6.5 | % | ASTM D4441 |
-- -- |
6.5 | % | ISO 8962 |
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
-- -- 2 |
2.21 | g/cm³ | ASTM D4895 , ISO 12086 |
-- -- 3 |
1.52 | g/cm³ | ISO 8962 , ASTM D4441 |
pH值 PH value |
|||
-- -- |
10.0 | ASTM E70 | |
-- -- |
ISO 1148 | ||
固体含量 - % PTFE by weight Solid content -% PTFE by weight |
|||
-- -- |
% | ASTM D4441 | |
-- -- |
% | ISO 12086 | |
平均颗粒尺寸 Average particle size |
nm | 内部方法 | |
布络克菲尔德粘度 Brookfield viscosity |
|||
25℃ 25℃ |
mPa·s | ASTM D2196 | |
25℃ 25℃ |
mPa·s | ISO 2555 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 of Sintered Resin |
3 at 60% solids |
【新闻资讯】查看全部
纳米多孔膜资料新分解方法研发中
2016-05-12 中国研究人员参与的一个研究团队研发出纳米多孔膜材料的新合成方法,据此制作出的高性能膜材料可实现高通量、高选择性的化学品分离,未来在石油化工行业、水处理与净化、反渗透海水淡化等领域有望实现更高效节能的应用。 英国帝国理工学院的团队2日在《自然・材料学》杂志网络版发表报告说,他们将近年来新研发的有机微孔高分子材料合成方法与传统成熟的界面聚合成膜工艺结合,成功制备出富含分子尺度孔道的超薄高分子膜。 研究人员说,核心技术是采用刚性且扭曲的有机单体分子,通过一步界面聚 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |