牌号简介 About |
---|
Lumicene MPE M 1810EP是一种以己烯为共聚单体的茂金属基线性低密度聚乙烯。与传统的LLDPE和其他茂金属基聚乙烯相比,鲁米新MPE M 1810EP的挤出压力低、气泡稳定性好、表观控制能力强,产量高。Lumicene MPE M 1810EP特别致力于薄膜应用,在这种应用中,需要优异的光学性能、优异的抗冲击性(即使在低温下)和密封强度,特别是在与LLDPE或LDPE的混合和共挤中。Lumicene MPE M 1810EP适用于消费、工业、食品或卫生包装领域的许多应用,如包装袋、深度冷冻、拉伸罩和层压。 Lumicene® mPE M 1810EP is a metallocene based Linear Low Density Polyethylene with hexene as comonomer. Lumicene® mPE M 1810EP can be processed at high output rates with low extrusion pressure, excellent bubble stability and gauge control in comparison with conventional LLDPE and other metallocene based polyethylene. Lumicene® mPE M 1810EP is especially dedicated to film applications where excellent optical properties in combination with outstanding impact resistance (even at low temperature) and sealing strength are required, particularly in blend and coextrusion with LLDPE or LDPE. Lumicene® mPE M 1810EP is suited for many applications in the field of consumer, industrial, food or hygiene packaging such as bags, deep freeze, stretch hood and lamination. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.917 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.0 | g/10min | ISO 1133 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
40 | µm | |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,屈服,40 µm,吹塑薄膜 MD, yield, 40 µ m, blow molded film |
10.0 | MPa | ISO 527-3 |
TD,屈服,40 µm,吹塑薄膜 TD, yield, 40 µ m, blow molded film |
10.0 | MPa | ISO 527-3 |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,断裂,40 µm,吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,断裂,40 µm,吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸应变 Tensile strain |
ISO 527-3 | ||
MD,断裂,40 µm,吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
% | ISO 527-3 | |
TD,断裂,40 µm,吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
% | ISO 527-3 | |
落锤冲击 Drop hammer impact |
|||
40 µm,吹塑薄膜 40 µ m, blow molded film |
g | ISO 7765-1 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ISO 6383-2 | ||
MD:40 µm,吹塑薄膜 MD: 40 µ m, blow molded film |
N | ISO 6383-2 | |
TD:40 µm,吹塑薄膜 TD: 40 µ m, blow molded film |
N | ISO 6383-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306 | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,40.0 µm,吹塑薄膜 45 °, 40.0 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
40 µm,吹塑薄膜 40 µ m, blow molded film |
% | ISO 14782 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
总投资约171.5亿元 中国神华煤制烯烃晋级项目获核准
2017-08-09 中国神华在8月7日晚间公告称,神华包头煤制烯烃升级示范项目获得内蒙古自治区发展和改革委员会的核准。项目主要建设规模为年产75万吨的煤制聚烯烃装置。其中,年产聚乙烯35万吨、聚丙烯40万吨。项目总投资约171.5亿元。 公告显示,项目单位为公司全资子公司神华包头煤化工有限责任公司(“包头煤化工公司”),建设地点为包头市九原工业园区。目前,包头煤化工公司已投产运营的煤制聚烯烃装置规模约为年产60万吨。其中,年产聚乙烯30万吨、聚丙烯30万吨。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
电邮一份说明书
PDF文档名:搜料网-TOTAL Polyethylene Lumicene® M 1810 EP证书
发送至:(多个地址,中间以逗号隔开)
发送一份副本给我:您还没有填写邮箱!(点击完善资料)