海索ES2202是一种未填充的环氧树脂体系,具有较高的工作温度和较长的使用寿命。建议在要求良好的耐化学性、高热变形温度和高湿度条件下良好的电气性能的地方使用。本产品推荐用于伺服定子、高温电阻、变压器和高温铸造形状。 HYSOL® ES2202™ is an unfilled epoxy system with a high operating temperature and long pot life. It is recommended for use where excellent chemical resistance, high heat distortion temperature and good electrical properties under high humidity conditions are required. This product is recommended for servo stators, high temperature resistors, transformers, and high temperature cast shapes. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
收缩率 Shrinkage rate |
|||
MD MD |
0.70 | % | |
吸水率 Water absorption rate |
|||
24hr 24hr |
0.11 | % | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
玻璃化转变温度 Glass transition temperature |
140 | ℃ | |
线性热膨胀系数 Linear coefficient of thermal expansion 2 |
|||
MD:< 140℃ MD:< 140℃ 2 |
6.5E-5 | 1/℃ | |
导热系数 Thermal conductivity coefficient |
0.19 | W/m/K | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
|||
-- -- 3 |
ohms | ||
-- -- 4 |
ohms | ||
-- -- 5 |
ohms | ||
体积电阻率 Volume resistivity |
|||
25 ℃ 25 ℃ |
ohms·cm | ||
85 ℃ 85 ℃ |
ohms·cm | ||
130 ℃ 130 ℃ |
ohms·cm | ||
介电强度 Dielectric strength |
|||
0.254 mm 0.254 mm |
kV/mm | ||
介电常数 Dielectric constant |
|||
25 ℃,100 Hz 25 ℃,100 Hz |
|||
25 ℃,1 kHz 25 ℃,1 kHz |
|||
25 ℃,10 kHz 25 ℃,10 kHz |
|||
25 ℃,100 kHz 25 ℃,100 kHz |
|||
85 ℃,100 Hz 85 ℃,100 Hz |
|||
85 ℃,1 kHz 85 ℃,1 kHz |
|||
85 ℃,10 kHz 85 ℃,10 kHz |
|||
85 ℃,100 kHz 85 ℃,100 kHz |
|||
130 ℃,100 Hz 130 ℃,100 Hz |
|||
130 ℃,1 kHz 130 ℃,1 kHz |
|||
130 ℃,10 kHz 130 ℃,10 kHz |
|||
130 ℃,100 kHz 130 ℃,100 kHz |
|||
耗散因数 Dissipation factor |
|||
25℃,100 Hz 25℃,100 Hz |
|||
25℃,1 kHz 25℃,1 kHz |
|||
25℃,10 kHz 25℃,10 kHz |
|||
25℃,100 kHz 25℃,100 kHz |
|||
85℃,100 Hz 85℃,100 Hz |
|||
85℃,1 kHz 85℃,1 kHz |
|||
85℃,10 kHz 85℃,10 kHz |
|||
85℃,100 kHz 85℃,100 kHz |
|||
130℃,100 Hz 130℃,100 Hz |
|||
130℃,1 kHz 130℃,1 kHz |
|||
130℃,10 kHz 130℃,10 kHz |
|||
130℃,100 kHz 130℃,100 kHz |
|||
耐电弧性 Arc resistance |
sec | ||
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
重量混合比(PBW) Weight Mix Ratio (PBW) |
|||
Part A Part A |
|||
Part B Part B |
|||
体积混合比(PBV) Volume Mixing Ratio (PBV) |
|||
Part B Part B |
|||
密度 Density |
|||
25℃ 25℃ 6 |
g/cm³ | ||
25℃ 25℃ 7 |
g/cm³ | ||
粘度 viscosity |
|||
布络克菲尔德 RVF,25℃ Brookfield RVF, 25 ℃ 8 |
Pa·s | ||
25℃ 25℃ |
Pa·s | ||
布络克菲尔德 RVF,25℃ Brookfield RVF, 25 ℃ 9 |
Pa·s | ||
胶凝时间 Gelation time |
|||
121℃ 121℃ 10 |
min | ||
40℃ 40℃ 11 |
min | ||
100℃ 100℃ 11 |
min | ||
储存稳定性 storage stability 11 |
|||
25 ℃ 25 ℃ 11 |
min | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
|||
拉伸强度 tensile strength |
MPa | ||
弯曲强度 bending strength |
MPa | ||
压缩强度 compressive strength |
MPa |
备注 |
---|
2、Alpha 1 |
3、25°C |
4、85°C |
5、130°C |
6、Part B |
7、Part A |
8、Part B, Spindle 2, speed 20 rpm |
9、Part A, Spindle 5, speed 10 rpm |
10、10 g mass |
11、200 g mass |
【新闻资讯】查看全部
黎巴嫩发电厂附近石油设施发生巨大火灾
2021-10-13 搜料网资讯: 据The New Arab 10月11日消息,在黎巴嫩南部的Zahrani石油设施中,一个汽油罐发生了大火。 据当地媒体报道,周一在黎巴嫩南部靠近该国主要发电厂之一的一家石油设施发生重 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |